Abstract:Steel slag with different basicity was prepared by the high temperature remelting method using converter steel slag as raw material. Slag-H2O/CO2 oxidation was carried out to produce H2/CO gas energy, as well as improve the magnetic properties of slag and increase the comprehensive utilization rate of slag. It was found that the main precipitated phases changed from olivine to magnesia rhodonite and finally to dicalcium silicate with the increasing basicity. And the RO phase had gradually exsolved from the main phase. With the same ferrous iron content, the slag with high basicity can greatly promote the oxidation reaction efficiency. The maximum gas production of the slag sample with a basicity of 1.83 was H2 (32.3 cm3/g) and CO (22.1 cm3/g), and the conversion rate reached 83.7%, 57% and it was only 40.5% and 32% respectively for the basicity of 1.13. The magnetic separation efficiency of oxidized slag samples was improved and it increased from 14.85% to 78.75% for the sample with basicity of 2.13.
李向阳, 李鹏, 国宏伟, 闫炳基. 低碱度含FeO渣热分解H2O/CO2制取H2/CO[J]. 中国冶金, 2021, 31(6): 101-107.
LI Xiang-yang, LI Peng, GUO Hong-wei, YAN Bing-ji. Preparation of H2/CO based on thermal decomposition of H2O/CO2 by slag containing FeO with low basicity[J]. China Metallurgy, 2021, 31(6): 101-107.
ZHAO J, YAN P, WANG D. Research on mineral characteristics of converter steel slag and its comprehensive utilization of internal and external recycle[J]. Journal of Cleaner Production, 2017, 156(10):50.
WANG G, WANG Y, GAO Z. Use of steel slag as a granular material: Volume expansion prediction and usability criteria[J]. Journal of Hazardous Materials, 2010, 184(1/2/3):555.
Liu C, Huang S, Blanpain B, et al. Optimization of mineralogy and microstructure of solidified basic oxygen furnace slag through SiO2 addition or atmosphere control during hot-stage slag treatment[J]. Metallurgical and Materials Transactions B, 2018, 50(1):210.
[12]
Gautier M, Poirier J, Franoise Bodénan, et al. Basic oxygen furnace (BOF) slag cooling: Laboratory characteristics and prediction calculations[J]. International Journal of Mineral Processing, 2013, 123:94.
[13]
Belhadj E, Cécile Diliberto, André Lecomte. Characterization and activation of basic oxygen furnace slag[J]. Cement and Concrete Composites, 2012, 34(1):34.
XUE Peng, HE Dong-feng, XU An-jun, et al. Modification of industrial BOF slag: Formation of MgFe2O4 and recycling of iron[J]. Journal of Alloys and Compounds,2017,712:640.
SUN Y Q, ZHANG Z T. Disposal of high temperature slags: A review of integration of heat recovery and material recycling[J]. Metallurgical and Materials Transactions:E. 2016, 3(3): 114.