Research Progressing for Longitudinal SurfaceCracks on Thin Slab
GAO Zhong,ZHANG Xingzhong,YAO Shufang
National Engineering and Research Center for Continuous Casting Technology, CentralIron and Steel Research Institute, Beijing 100081,China
摘要 薄板坯表面纵裂是连铸连轧生产线上的严重质量缺陷。分析了薄板坯表面纵裂的成因;总结了薄板坯表面纵裂的特征、影响因素及其防止纵裂的措施;提出了今后研究纵裂纹的方向。
关键词 :
薄板坯连铸 ,
纵裂纹 ,
成因 ,
措施
Abstract :The longitudinal surface crack on thin slab is a serious quality defect at thin slab continuous casting and rolling process. According to technical literature, the factors influencing surface longitudinal crack formation are very complex. Crack formation is analyzed, crack characteristics, influencing affects and controlling measures of surface longitudinal crack during casting process are summarized. The aspect of researching longitudinal surface crack is pointed out.
Key words :
thin slab continuous casting
longitudinal surface crack
causes
measures
收稿日期: 1900-01-01
[1]
薛锴,刘新军,张宇晓,司晋利,董江峰,霍瑞霞. 高炉鼓风机高效安全运行措施的实践 [J]. , 2014, 24(09): 53-56.
[2]
张健,汪灵俐,张宇,刘银梅,韩自博. 浅析热闷钢渣加工生产线粉尘的控制措施 [J]. , 2014, 25(07): 64-66.
[3]
王玉生, 唐文明, 何顺生, 田晓涛, 于博. 250 t 转炉LT泄爆控制的生产实践 [J]. Journal of Materials Sciences & Technology, 2013, 23(3): 33-35.
[4]
姜杉杉, 王代军. 四川德胜260 m2 烧结工程设计及提高烧结矿强度生产实践 [J]. Journal of Materials Sciences & Technology, 2013, 23(2): 29-33.
[5]
田 蜜, 李海洋. 武钢200 t转炉“负能炼钢”技术的开发及应用 [J]. Journal of Materials Sciences & Technology, 2013, 23(2): 37-39.
[6]
刘振林, 刘崇亭, 贾 勇, 刘继彬. 济钢近几年炼铁系统技术创新与实践 [J]. Journal of Materials Sciences & Technology, 2012, 22(6): 8-11.
[7]
王 谦, 鲁永剑 , 何宇明, 胡 兵, 熊银成, 张建国. 提高宽厚板坯无清理率的关键技术 [J]. Journal of Materials Sciences & Technology, 2012, 22(12): 22-27.
[8]
吕亚,王新志,李文山,刘磊,胡锐,张书铭. 超宽板坯表面纵裂纹的原因分析及预防措施 [J]. Journal of Materials Sciences & Technology, 2011, 21(6): 19-22.
[9]
王立君, 李法兴, 张君平, 时振明. 提高电炉流程生产含硼钢冶金质量的措施 [J]. Journal of Materials Sciences & Technology, 2011, 21(3): 24-27.
[10]
王柱, 刘宁, 李文, 李银军, 田勇. 济钢1700热连轧粗轧机打滑现象研究 [J]. Journal of Materials Sciences & Technology, 2011, 21(1): 38-42.
[11]
刘文仲. 中国钢铁工业过程控制数学模型的应用现状及对策 [J]. Journal of Materials Sciences & Technology, 2010, 20(12): 1-3.
[12]
彭其春, 赵金涛, 田俊, 陈永金, 张学辉, 彭胜堂. 武钢冷轧板表面“黑线”缺陷分析 [J]. Journal of Materials Sciences & Technology, 2010, 20(1): 21-25.
[13]
李聿军,许宁辉,李斌,何裕发,向华,邵三萍. 小型转炉降低钢铁料消耗的生产实践 [J]. Journal of Materials Sciences & Technology, 2008, 18(8): 28-28.
[14]
孙彦辉1 ,赵长亮1 ,蔡开科1 ,杨素波2 ,陈永3 ,李桂军3 ,顾武安3. 连铸板坯表层网状裂纹的成因研究 [J]. Journal of Materials Sciences & Technology, 2008, 18(4): 15-15.
[15]
崔风平1 ,赵乾2 ,唐愈3. 铸坯内部缺陷对钢板分层形成的影响 [J]. Journal of Materials Sciences & Technology, 2008, 18(2): 14-14.