辉钼矿湿法冶金研究进展

doi:10.13228/j.boyuan.issn1006-9356.20220702

摘要
图/表
参考文献
相关文章 (10)

全文: PDF (1431 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要辉钼矿(MoS₂)是一种重要的含钼矿石,目前80%左右的钼来源于此类资源。工业上通常采用浮选-火法冶金工艺生产钼金属,然而该传统工艺易产生SO₂而造成环境污染,且存在回收率低、难以处理低品位矿石等问题。与之相比,湿法冶金因具备经济、环保、高效等优势而备受关注。为此,综合分析了近年来辉钼矿浸出技术的发展现状和前景,比较了不同钼分离提取方法的优缺点。通过分析指出,未来辉钼矿湿法冶金技术发展的核心在于浸出,利用开发新技术和优化条件实现高效钼浸出、通过缩短流程并实现工业化应用、提高伴生资源的同步回收等将成为重点研究方向。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	作者相关文章
	姜丽帅
	韩百岁
	冷红光
	杨孟月
	李潇煜

关键词 ：辉钼矿, 钼冶金, 浸出, 萃取, 离子交换

Abstract：Molybdenite (MoS₂) is an important molybdenum-bearing ore. At present, about 80% of molybdenum comes from this kind of resources. In industry, flotation-pyrometallurgical process is usually used to produce molybdenum metal. However, this traditional process is easy to produce SO₂ and cause environmental pollution, and there are some problems, such as low recovery rate, difficult to deal with low grade ore and so on. In contrast, hydrometallurgy has attracted much attention because of its advantages such as economy, environmental protection, high efficiency and so on. For this reason, the development and prospect of molybdate leaching technology in recent years are comprehensively analyzed, and the advantages and disadvantages of different molybdenum separation and extraction methods are compared. It is pointed out that leaching is the core of future development for molybdate hydrometallurgy technology. Developing new technologies and optimizing conditions to achieve efficient molybdenum leaching, shortening the process and achieving industrial application, and improving the synchronous recovery of associated resources will become the key research direction.

Key words： molybdenite molybdenum metallurgy leaching extraction ion exchange

收稿日期: 2022-08-30

基金资助:2021年度校优秀青年人才项目(2021YQ05)

通讯作者: 韩百岁(1987—), 男, 博士, 副教授; E-mail: baisui.han@ustl.edu.cn

作者简介: 姜丽帅(1998—), 男, 硕士生; E-mail: 3078877981@qq.com

引用本文:

姜丽帅, 韩百岁, 冷红光, 杨孟月, 李潇煜. 辉钼矿湿法冶金研究进展[J]. 中国冶金, 2023, 33(2): 22-30. JIANG Li-shuai, HAN Bai-sui, LENG Hong-guang, YANG Meng-Yue, LI Xiao-yu. Research progress of hydrometallurgy of molybdenite[J]. China Metallurgy, 2023, 33(2): 22-30.

链接本文:

http://www.zgyj.ac.cn/CN/10.13228/j.boyuan.issn1006-9356.20220702 或 http://www.zgyj.ac.cn/CN/Y2023/V33/I2/22

[1]	雷锐. 钼金属深加工产品现状及技术应用分析[J]. 世界有色金属, 2018(19): 288.
[2]	李红. 解读钼金属深加工产品现状及具体技术应用[J]. 世界有色金属, 2019(8): 163.
[3]	杨双平,刘守满,王苗,等.含钼废渣冶炼钼铁的优化试验[J].中国冶金,2022,32(5):131.
[4]	殳黎平,朱施利,胡文豪,等.含钼双相钢DP600相变研究和工艺实践[J].中国冶金,2018,28(6):43.
[5]	陈旭. 铜钼混合精矿铜钼分离抑制剂的选择试验研究[D]. 沈阳:东北大学, 2012.
[6]	刘奇英. 铜钼分离抑制剂巯基乙酸钠合成工艺研究[D]. 西安:西北大学, 2010.
[7]	黄瑞强,阮英华,雷主生,等. 丰山铜矿铜钼分离抑制剂D8应用小型试验研究[J]. 矿冶, 2014, 23(6): 22.
[8]	刘水红,王立刚,李成必,等. 某铜钼矿提高钼回收率选矿试验研究[J]. 中国矿业, 2014, 23(增刊2): 284.
[9]	刘鹏. 新型巯基乙酸钠抑制剂在铜钼分离中的应用[J]. 世界有色金属, 2016 (20): 180.
[10]	李明阳. 抑制剂分子构型对铜钼分离影响的机理研究[D]. 沈阳:东北大学, 2017.
[11]	王剑. 西藏某复杂铜钼混合精矿浮选分离及铜抑制剂的试验研究[D]. 沈阳:东北大学, 2016.
[12]	肖军辉,施哲,陈金花. 含钼铜精矿氧化焙烧-浸出分离钼研究[J]. 重庆大学学报, 2016, 39(4): 50.
[13]	王璐,李梦超,阙标华,等. 辉钼精矿的氧化焙烧[J]. 中国有色金属学报, 2021, 31(7): 1952.
[14]	李相良,王政,王玉芳,等. 辉钼矿氧化焙烧试验研究[J]. 中国资源综合利用, 2017, 35(9): 29.
[15]	杜国山,邱爽,李少华. 钼精矿多膛炉焙烧节能分析及改造[J]. 有色冶金节能, 2016, 32(2): 27.
[16]	王海北,李贺,王玉芳. 稀贵金属加压浸出技术现状及展望[J]. 有色金属(冶炼部分), 2021 (6): 1.
[17]	牟文宁,张鸿彪,苏志强,等. 低品位钼矿钠化焙烧-水浸过程钼的转化研究[J]. 稀有金属, 2015, 39(9): 854.
[18]	朱永明,张飒,张生旭. 某铜钼矿选矿及尾矿水回用试验研究[J]. 矿业研究与开发, 2021, 41(10): 132.
[19]	Ramesh A, Hasegawa H, Sugimoto W, et al. Adsorption of gold(iii), platinum(iv) and palladium(ii) onto glycine modified crosslinked chitosan resin[J]. Bioresource Technology, 2008, 99(9):3801.
[20]	赵睿. 辉钼矿基抗坏血酸与葡萄糖电化学传感器的制备及应用[D]. 鞍山:辽宁科技大学, 2020.
[21]	Vizsolyi A, Peters E. Nitric acid leaching of molybdenite concentrates[J]. Elsevier, 1980, 6(1):103.
[22]	Khoshnevisan A, Yoozbashizadeh H, Mozammel M, et al. Kinetics of pressure oxidative leaching of molybdenite concentrate by nitric acid[J]. Hydrometallurgy, 2011, 111(1):52.
[23]	李飞,张文娟,陈星宇. 常温常压下辉钼矿硝-硫酸浸出动力学[J]. 中国有色金属学报, 2016, 26(11): 2420.
[24]	Smirnov K M, Raspopov N A, Shneerson Y M, et al. Autoclave leaching of molybdenite concentrates with catalytic additives of nitric acid[J]. Russian Metallurgy (Metally), 2010, 2010(7):588.
[25]	MU W, ZHANG T, LÜ G, et al. Transformation behavior of molybdenum during pressure oxidation process of molybdenite concentrate[C]//Proceedings of 2011 International Conference on Chemical, Mechanical and Materials Engineering(CMME2011). Venice: Trans Tech Publications,2011: 268.
[26]	陈庆根. 钼精矿热压碱浸-离子交换提取钼试验研究[J]. 矿产综合利用, 2014(4): 40.
[27]	彭建蓉,杨大锦,陈加希,等. 原生钼矿加压碱浸试验研究[J]. 稀有金属, 2007(增刊1): 110.
[28]	程光荣,马秀华,王述吉,等. 用压热浸出和溶剂萃取技术生产钼酸铵[J]. 湿法冶金, 1994(3): 27.
[29]	宋成盈,宋会娟,王建设,等. 氧气氧化法分解辉钼矿[J]. 金属矿山, 2009 (3): 69.
[30]	卜春阳,曹维成,王璐,等. 辉钼矿冶炼工艺综述及展望[J]. 中国钼业, 2017, 41(6): 5.
[31]	LIU You-cai, ZHONG Hong, CAO Zhan-fang. Molybdenum removal from copper ore concentrate by sodium hypochlorite leaching[J]. Mining Science and Technology (China), 2010, 21(1): 61.
[32]	柯家骏. 辉钼矿氧化浸取动力学研究[J]. 稀有金属, 1984 (1): 6.
[33]	LIU W, XU H, YANG X, et al. Extraction of molybdenum from low-grade Ni-Mo ore in sodium hypochlorite solution under mechanical activation[J]. Minerals Engineering, 2011, 24(14):1580.
[34]	顾珩,李洪桂,刘茂盛. 辉钼矿湿法浸出新工艺研究[J]. 中国钼业, 1997 (5): 30.
[35]	符剑刚. 采用软锰矿强化辉钼矿的氧化分解及联产钼酸铵与硫酸锰[D]. 长沙:中南大学, 2009.
[36]	谢素玲. 高性能多用途的DSA阳极[J]. 电镀与涂饰, 2004,(3): 30.
[37]	曹占芳,钟宏,邱朝辉,等. 缓冲体系中辉钼矿电氧化浸出研究[J]. 现代化工, 2009, 29(增刊1): 16.
[38]	贾丽娟. 辉钼矿超声电氧化分解新工艺的研究[D]. 长沙:中南大学, 2008.
[39]	闻振乾. 辉钼矿电氧化分解过程的研究[D]. 长沙:中南大学, 2009.
[40]	徐海清,刘代云,刘慧勇. 电氧化湿法分解钼中矿工艺[J]. 过程工程学报, 2010, 10(3): 554.
[41]	吴贤,李来平,张新,等. 用矿浆电解法分解辉钼矿试验研究[J]. 现代矿业, 2009, 25(10): 61.
[42]	曹占芳,钟宏,刘广义. 墨西哥某铜矿浮选-浸出-萃取-电积回收铜工艺研究[J]. 金属矿山, 2008(5): 63.
[43]	符剑刚,贾丽娟,钟宏. 超声电氧化分解辉钼矿电解槽体系的设计研究[J]. 稀有金属与硬质合金, 2007(3): 5.
[44]	王军,陶浪,甘晓文,等. 含银固体废弃物催化黄铜矿微生物浸出研究[J]. 矿冶工程, 2016, 36(3): 66.
[45]	邓莎,刘兆悦,杨玮,等. 含砷金矿微生物预氧化过程强化方法研究进展[J]. 矿产保护与利用, 2021, 41(6): 150.
[46]	李导远. 巨大芽孢杆菌浸出金矿实验研究[D]. 包头:内蒙古科技大学, 2021.
[47]	Olson G J, Clark T R. Bioleaching of molybdenite[J]. Hydrometallurgy, 2008, 93(1):10.
[48]	黄明清,王贻明,杨保华,等. 辉钼矿生物浸出研究进展[J]. 中国钼业, 2011, 35(4): 14.
[49]	上官若凡,郝瑛轩,张湛博. 钼尾矿中钼、铜和铁的生物浸出实验研究[J]. 矿冶工程, 2019, 39(4): 119.
[50]	Abdollahi H, Zshafaei S, Oaparast M.N, et al. Bio-dissolution of Cu, Mo and Re from molybdenite concentrate using mix mesophilic microorganism in shake flask[J]. Transactions of Nonferrous Metals Society of China, 2013, 23(1): 219.
[51]	吉兆宁,余斌,刘坚,等. 金堆城低品位钼矿石可浸性研究[J]. 有色金属(矿山部分), 2002(5): 15.
[52]	Wolfgang Kummer, Wilfried Gutknecht, James Gregory Olson, et al. Recovery of molybdenum from molybdenum bearing sulfide materials by bioleaching in the presence of iron: US,US8268037[P].2012-09-18.
[53]	Orlando Y, Eugenia A, Rodrigo Y, et al. The role of solar energy (uv-vis-nir) as an assistant for sulfide minerals leaching and its potential application for metal extraction[J]. Minerals, 2021, 11(8):828.
[54]	徐芳苓. 钼酸铵生产线水洗废水中钼回收的研究[J]. 化工管理, 2017(5): 229.
[55]	张帅,张华,冯培忠. 钼资源回收工艺现状及展望[J]. 无机盐工业, 2011, 43(12): 12.
[56]	王磊,周新文,唐丽霞. 离子交换树脂从酸性废水中回收钼的研究[J]. 中国钼业, 2015, 39(4): 48.
[57]	曹占芳. 辉钼矿湿法冶金新工艺及其机理研究[D]. 长沙:中南大学, 2010.
[58]	邱朝辉. 钼、铼的萃取与离子交换分离研究[D]. 长沙:中南大学, 2010.
[59]	张文轩. 氯酸盐湿法氧化分解辉钼矿新工艺及机理研究[D]. 长沙:中南大学, 2009.
[60]	姚琳,邓桂春. 含钼的酸性料液中回收钼的研究[J]. 辽宁大学学报(自然科学版), 2011, 38(2): 111.
[61]	吴江丽. 辉钼矿和二氧化锰共同焙烧新工艺的研究[D]. 长沙:中南大学, 2005.
[62]	刘泉,陆明杰,汪慧刚,等. 用双功能性离子液体[A336][P204]从硫酸体系中萃取钼[J]. 湿法冶金, 2020, 39(6): 507.
[63]	CAO Z, ZHONG H, QIU Z, et al. A novel technology for molybdenum extraction from molybdenite concentrate[J]. Hydrometallurgy, 2009, 99(1):2.
[64]	白晓娟. 铼钼铜高效综合回收萃取工艺研究[D]. 杭州:浙江大学, 2022.
[65]	李建,刘建. 磷类萃取剂萃取钼(Ⅵ)的性能研究[J]. 湿法冶金, 2007(3): 146.
[66]	Ali E, Dariush A, Anatolyevich N P, et al. Selective recovery of molybdenum over rhenium from molybdenite flue dust leaching solution using Pc88a extractant[J]. Metals, 2020, 10(11): 1423.
[67]	罗嵩. 从辉钼矿尾矿中回收钼的实验研究[D]. 沈阳:东北大学, 2008.
[68]	宁阳坤. 离子交换法回收钼冶炼废酸中钼和铼研究[D]. 郑州: 郑州大学, 2018.
[69]	LAN X, LIANG S, SONG Y. Recovery of rhenium from molybdenite calcine by a resin-in-pulp process[J]. Hydrometallurgy, 2006, 82(3): 133.
[70]	吕改芳. 钼焙烧烟气吸收液提铼制备高铼酸钾[D]. 沈阳:辽宁大学, 2011.
[71]	刘红召,曹耀华,高照国. 辉钼矿焙烧烟气淋洗液中铼的富集[J]. 有色金属(冶炼部分), 2009(6): 39.
[72]	付云枫. 氧压水浸法分解辉钼矿提取分离钼硫资源的应用基础研究[D]. 北京:中国科学院大学(中国科学院过程工程研究所):2018.
[73]	周新文,王磊,唐丽霞. 离子交换法除杂制备钼酸铵[J]. 中国钼业, 2011, 35(3): 33.