Abstract：The occurrence mechanism of intermediate crack in slab was discussed on the basis of the experiment data of 100 t ConverterLFCC production line. The results showed that the bulging strain and roller gap shrinking strain were the outer causes of the intermediate crack. The high temperature mechanical property of steel was determined by its chemical component, which caused the intermediate crack. The intermediate crack was the interaction of bulging strain and roller gap shrinking strain and the high temperature mechanical property of steel. And the bending strain and straightening strain had very important effect on the propagation of intermediate crack in CC slab, which may cause the extension of intermediate crack. Reasonable roller gap design combined with the steel grade and specification was very important for the control of the intermediate crack in slab.
王国连，曹磊. 宽厚板连铸坯中间裂纹成因分析及控制[J]. 中国冶金, 2017, 27(10): 54-58.
WANG Guolian，CAO Lei. Cause analysis and control of intermediate crack in wide and heavy plate continuous castiong slab. China Metallurgy, 2017, 27(10): 54-58.
WANG Hongfeng, SONG Jingxin, ZOU Junsu．Forming and control of center crack in slab cast [J]． Continuous Casting,2002,(6):36-37．
[6]
PAN Zhiguo，YI Guilan． The Analysis and Controlling Measure for the Longitudinal Crack of Continuous Casting Slab[Z]． Symposium of the 12th National Steel-Making Conference，Beijing：2000．
2017, Vol. 27 