Research and Application of Oxidation-Resistance Technology for Slab in Laisteel Group
LI Guang-yan1,SHANG Fu-cheng2,WEI Cheng-zhi1,HE Xiao-wen1
(1.Laisteel Group R&D Center, Laiwu 271104, Shandong, China
2.The Energy and Enviroment Protection Dept.of Laiwu Iron and Steel Group Company, Laiwu 271104, Shandong, China)
The anti-oxidation mechanism and corrosion protection principle at high temperature were studied in the laboratory. The coating sample and the normal hot-transporting slab were fed into the reheating furnace, to systematically analyze the temperature change and surface change of the slabs within the process from continuous casting to reheating furnace, especially to investigate its oxidation state. The anti-oxidation formula of slab in Laigang and the implementation method of spraying were studied to reduce the oxiding loss of slabs in the reheating furnace and enhance the yield of slabs. At last, the formula of anti-oxidation coating was confirmed and the corresponding test was carried out. The result shows that the coating slab not only has no influence on the rolling schedule, but also its surface oxidation is reduced and the surface quality of steel products is improved.
李广艳,商福成,魏承志,何孝文. 莱钢钢坯防氧化的研究与应用[J]. 中国冶金, 2014, 24(2): 14-18.
LI Guang-yan,SHANG Fu-cheng,WEI Cheng-zhi,HE Xiao-wen. Research and Application of Oxidation-Resistance Technology for Slab in Laisteel Group. China Metallurgy, 2014, 24(2): 14-18.