鞍钢高炉喷吹除尘灰的研究与应用
张立国, 王再义, 刘德军, 张 伟, 王相力
鞍钢股份有限公司,辽宁鞍山 114009
Study and Application of Dust Injection Into BF
摘要 阐述了鞍钢目前高炉除尘灰产生的工艺流程和利用方式,对除尘灰的化学成分、粒度组成进行了分析,并 对喷吹煤粉中添加除尘灰进行实验室研究,分析了配入不同比例除尘灰后,混合煤粉的工业分析、灰熔融性能、发 热值和燃烧性能的变化情况,开展喷吹煤粉中配入除尘灰的工业试验,寻求适合配入比例,并对高炉喷吹除尘灰后 的炉况的变化及喷吹除尘灰的优缺点进行说明,得出鞍钢在目前的生产条件下,高炉可以进行除尘灰的喷吹应用。
关键词 :
高炉 ,
除尘灰 ,
喷煤比 ,
回旋区
Abstract :The prosess of BF dust and utilization mode were introduced in this paper. The composition and particle size of BF dust was analyzed in laboratory. The mixture of BF dust with pulverous coal was studied in content of ash, volatile and fixed carbon. The industry test was conducted to find best mixing proportion and to observe the condition change in BF. It can be concluded that dust injection in BF is feasible under present producing condition in Ansteel.
Key words :
blast furnace
dust
coal ratio
rotary region
收稿日期: 2012-03-12
出版日期: 2012-10-15
通讯作者:
张立国
E-mail: zlg3960847@163.com
[1]
安波 ,岳强 姚应林,柯显峰. 基于低成本炼铁过程控制的研究实践 [J]. , 2014, 24(5): 35-39.
[2]
秦晓勇 ,刘雄 ,陈林根 ,孙丰瑞 . 高炉利用系数目标优化模型的研究与应用 [J]. , 2014, 24(4): 5-10.
[3]
张殿伟 ,赵志星,赵宝军. 首钢高炉渣与配制四组元渣的黏度研究 [J]. , 2014, 24(4): 11-15.
[4]
芦永明,田乃媛,贺东风,王丽娜,陈宏志. 全板带型钢厂高炉—转炉区段配置及其生产组织探讨 [J]. , 2014, 24(4): 45-50.
[5]
孟祥龙,张福明,曹朝真. 首钢高炉喷煤技术发展与创新 [J]. , 2014, 24(3): 21-26.
[6]
王冬青,马泽军,竺维春. 喷吹煤Y在首钢高炉的应用 [J]. , 2014, 24(3): 48-51.
[7]
周飞,俞金城,彭黎明. 安徽长江钢铁公司3号1080m3高炉喷煤设计特点 [J]. , 2014, 24(11): 58-62.
[8]
芮文杰,唐章富,刘向新. 邯钢2×60MW常规机组升级CCPP方案 [J]. , 2014, 24(10): 32-34.
[9]
李胜杰,张希刚,赵恒山. 安钢2号高炉经济块矿生产实践与成本分析 [J]. , 2014, 24(10): 39-41.
[10]
杜斯宏,宋剑,吴亚明,曾华锋. 攀钢钒新3号高炉年修开炉快速达产实践 [J]. , 2014, 24(1): 18-22.
[11]
邱国兴,殷忠力,朱化朋,姜智文. 提高煤气利用率降低高炉燃料比 [J]. , 2014, 24(1): 47-51.
[12]
高建军 严定鎏 齐渊洪 张俊 郭玉华. 氧气高炉风口前燃烧带数值模拟 [J]. , 2014, 24(09): 44-48.
[13]
唐小辉,刘润藻,李士琦,杨静波,肖宏,寿庆霞. 唐钢高炉瓦斯灰的提铁提锌试验 [J]. , 2014, 24(09): 49-52.
[14]
薛锴,刘新军,张宇晓,司晋利,董江峰,霍瑞霞. 高炉鼓风机高效安全运行措施的实践 [J]. , 2014, 24(09): 53-56.
[15]
姜华,蔡九菊. 高炉炉缸用后炭砖中脆化层的研究 [J]. , 2014, 24(09): 57-62.