高炉炉渣脱硫能力分析
谢皓,王劲松,邹忠平,王刚,徐小辉
重庆赛迪冶炼装备系统集成工程技术研究中心有限公司炼铁研究室, 重庆 401122
Analysis of the desulphurization capacity of blast furnace slag
XIE Hao,WANG Jin-song,ZOU Zhong-ping,WANG Gang,XU Xiao-hui
Ironmaking Department of CISDI Research and Development Co.,Ltd., Chongqing 401122, China)
摘要 为研究高炉炉渣脱S能力、降低铁水含S量,针对某高炉S负荷进行来源分析,对其炉渣数据进行了热力学分析,得到了铁水Si含量、炉渣碱度以及出铁速度对炉渣脱S能力的影响规律,并提出了改善炉渣脱S能力的措施。
关键词 :
高炉 ,
炉渣 ,
脱硫能力
Abstract :The source of sulfur of a certain blast furnace was analyzed and slag data was analyzed by thermodynamic method in order to study the desulphurization capacity of blast-furnace slag and reduce the sulfur content in molten iron. The influence rules of Si content, slag basicity as well as the tapping speed on desulphurization capacity were obtained by the analysis. Measures to improve the slag desulphurization capacity were also put forward.
Key words :
blast furnace
slag
desulphurization capacity
收稿日期: 2014-02-18
出版日期: 2014-12-22
通讯作者:
谢皓
E-mail: xiehao_1984@sina.com.cn
[1]
安波 ,岳强 姚应林,柯显峰. 基于低成本炼铁过程控制的研究实践 [J]. , 2014, 24(5): 35-39.
[2]
秦晓勇 ,刘雄 ,陈林根 ,孙丰瑞 . 高炉利用系数目标优化模型的研究与应用 [J]. , 2014, 24(4): 5-10.
[3]
张殿伟 ,赵志星,赵宝军. 首钢高炉渣与配制四组元渣的黏度研究 [J]. , 2014, 24(4): 11-15.
[4]
芦永明,田乃媛,贺东风,王丽娜,陈宏志. 全板带型钢厂高炉—转炉区段配置及其生产组织探讨 [J]. , 2014, 24(4): 45-50.
[5]
孟祥龙,张福明,曹朝真. 首钢高炉喷煤技术发展与创新 [J]. , 2014, 24(3): 21-26.
[6]
王冬青,马泽军,竺维春. 喷吹煤Y在首钢高炉的应用 [J]. , 2014, 24(3): 48-51.
[7]
赵贵希,刘其敏. 高炉碱负荷和锌负荷的来源透析及对策 [J]. , 2014, 24(12): 51-54.
[8]
周飞,俞金城,彭黎明. 安徽长江钢铁公司3号1080m3高炉喷煤设计特点 [J]. , 2014, 24(11): 58-62.
[9]
芮文杰,唐章富,刘向新. 邯钢2×60MW常规机组升级CCPP方案 [J]. , 2014, 24(10): 32-34.
[10]
李胜杰,张希刚,赵恒山. 安钢2号高炉经济块矿生产实践与成本分析 [J]. , 2014, 24(10): 39-41.
[11]
杜斯宏,宋剑,吴亚明,曾华锋. 攀钢钒新3号高炉年修开炉快速达产实践 [J]. , 2014, 24(1): 18-22.
[12]
邱国兴,殷忠力,朱化朋,姜智文. 提高煤气利用率降低高炉燃料比 [J]. , 2014, 24(1): 47-51.
[13]
高建军 严定鎏 齐渊洪 张俊 郭玉华. 氧气高炉风口前燃烧带数值模拟 [J]. , 2014, 24(09): 44-48.
[14]
唐小辉,刘润藻,李士琦,杨静波,肖宏,寿庆霞. 唐钢高炉瓦斯灰的提铁提锌试验 [J]. , 2014, 24(09): 49-52.
[15]
薛锴,刘新军,张宇晓,司晋利,董江峰,霍瑞霞. 高炉鼓风机高效安全运行措施的实践 [J]. , 2014, 24(09): 53-56.