Relationship between Coke Reactivity and Strength after Reaction and Research of influence factor
YU Qing, WANG De-quan, WU Zi-liang, WANG Jian-guo, XU Feng
1. Ironworks of Laiwu Iron and Steel Co., Ltd., Laiwu 271104, Shandong, China
2. Ironworks of Laiwu Yinshan Profile Steel Co., Ltd., Laiwu 271104, Shandong, China
For better prediction of coke behavior in blast furnace,a great many of coke varieties were detected and their relevant data analyzed. The results shuow that the coke reactivity and its strength after reaction have negative relativity. The cold strength of coke and its thermal property was compared. It is suggested that coking enterprise should pay more attention on the thermal property of coke on condition that the coke strength is qualified. According to determination of reactivity and post-reaction strength of cok , the Influence factors H2O content, method of coke quenching, and material’s struture to the properties of Hard Cok is studied in this paper. The result showed that, H2O content of coke maintaining low level can inprove the Metallurgical properties; Dry quenching of coke can noteblely improve the property; Material’s struture and property can ultimately influence the property of coke.
于青, 王德全, 吴子良, 王建国, 许峰. 焦炭反应性和反应后强度的关系及影响因素研究[J]. 中国冶金, 2012, 22(3): 10-14.
YU Qing, WANG De-quan, WU Zi-liang, WANG Jian-guo, XU Feng. Relationship between Coke Reactivity and Strength after Reaction and Research of influence factor. China Metallurgy, 2012, 22(3): 10-14.