氮在炼钢及连铸过程中的变化及影响因素分析
杨之俊, 杨海滨, 王彦杰
河北钢铁集团邯钢三炼钢厂,河北 邯郸 056015
Investigation on the Behavior of Nitrogen in the Steel Making and Continuous Casting Process and its Influence Factors
摘要 <介绍了邯钢三炼钢厂从炼钢到连铸生产过程中[N]的变化情况,通过理论分析及生产试验研究影响[N]变化的各种因素,提出了降低[N]含量的改进措施,在生产实践中取得了明显的效果:连铸中间包钢水中[N]由平均54×10-6降低到平均43×10-6,同比降低20.4%。
关键词 :
氮 ,
顶底复吹 ,
精炼 ,
保护浇注
Abstract :In this article, the behavior of Nitrogen from steel making to casting has been investigated in steel making plant No.3 of Handan iron and steel Co., Ltd.. The various influence factors to the Nitrogen behavior have been analyzed and relevant countermeasures have been proposed to reduce the Nitrogen content in the steel. The results achieved in the production practice is remarkable. The Nitrogen content in steel of the tundish has decreased from an average of 54×10-6 to 43×10-6.
Key words :
nitrogen
top and bottom combined blowing
refining
protected casting
收稿日期: 2010-08-16
出版日期: 2011-04-20
通讯作者:
杨海滨
E-mail: yhb0427@163.com
参考文献:
[1]
张鉴.炉外精炼的理论与实践[M].北京:冶金工业出版社,2004.43—44.
[1]
高泽平,贺道中.炉外精炼[M].北京:冶金工业出版社,2005.39—40.
[2]
康永林,傅杰等.薄板坯连铸连轧钢的组织性能控制[M].北京:冶金工业出版社,2006.52—53.
[1]
卓伟伟,徐玉松. 涟钢90t顶底复吹转炉成渣路线 [J]. , 2014, 24(4): 22-25.
[2]
沈岸明,刘国庆. X80管线钢生产过程氮的控制实践 [J]. , 2014, 24(09): 39-43.
[3]
赵艳玲,王淑满,王洪兴,常立山. X80管线钢的生产实践 [J]. , 2014, 24(08): 26-29.
[4]
封波,徐昊,高卫,吴六顺,董元篪. LF精炼渣低氟化研究进展 [J]. , 2014, 24(06): 1-5.
[5]
刘志国, 王洪兴. 连铸保护浇注工艺改进 [J]. Journal of Materials Sciences & Technology, 2013, 23(8): 38-41.
[6]
张彩东, 杨晓江, 王 峰, 张大勇. 唐钢RH钢水洁净度分析与研究 [J]. Journal of Materials Sciences & Technology, 2013, 23(8): 9-13.
[7]
陆军, 郑良才, 杜建新. 电炉履带钢23MnBM氮控制的生产实践 [J]. Journal of Materials Sciences & Technology, 2013, 23(5): 38-40.
[8]
杨荣光, 王志刚. 超低硫钢精炼工艺生产实践 [J]. Journal of Materials Sciences & Technology, 2013, 23(5): 34-37.
[9]
成国光, 芮其宣, 秦哲, 张鉴 . 单嘴精炼炉技术的开发与应用 [J]. Journal of Materials Sciences & Technology, 2013, 23(3): 1-10.
[10]
杨利委. 短流程增氮工艺探讨 [J]. Journal of Materials Sciences & Technology, 2013, 23(12): 21-24.
[11]
翟冬雨, 方 磊, 蔡可森. 南钢高效益低成本转炉冶炼的工业研究 [J]. Journal of Materials Sciences & Technology, 2012, 22(8): 11-13.
[12]
陈 良 , 焦玉莉 , 黄优明. 20CrMnTiH齿轮钢可浇性研究与实践 [J]. Journal of Materials Sciences & Technology, 2012, 22(8): 40-43..
[13]
蔡开科,孙彦辉,田志红. 炼钢-精炼-连铸过程钢水超纯净度控制战略 [J]. Journal of Materials Sciences & Technology, 2012, 22(4): 1-7.
[14]
黄建军, 张新文, 周 伟, 杜志明. 37Mn-1铸坯表面气孔缺陷分析与研究 [J]. Journal of Materials Sciences & Technology, 2012, 22(2): 19-24.
[15]
鞠艳美, 张 伟, 李法兴. 油井管用非调质钢36Mn2V冶金质量控制技术 [J]. Journal of Materials Sciences & Technology, 2012, 22(12): 17-20.