连铸板坯三角区裂纹成因分析及改进措施
修立策
济南钢铁集团总公司第三炼钢厂, 山东 济南 250101
Formation Mechanism and Control of Triangular Area Crack of Continuous Casting Slab
XIU Lice
No.3 Steel Making Plant, Jinan Iron and Steel Co.Ltd, Jinan 250101, Shandong, China
摘要 通过对铸坯的低倍检验和三角区裂纹部位的电镜扫描,分析了连铸板坯三角区裂纹的类型和成因;提出了从钢水成分、二冷配水、驱动压力、轻压下、支撑段等方面的改进措施。其结果表明,钢中硫和铸坯的支撑段是影响三角区裂纹的主要因素。具体措施的实施,使三角区裂纹的发生率和级别大幅度下降。
关键词 :
连铸板坯 ,
三角区裂纹 ,
支撑段 ,
硫 ,
低倍检验
Abstract :The type and formation of the triangular area cracks of the continuous casting slab were analyzed though macro examination and scanning the cracks by SEM. The measures to reduce the triangular area cracks were put forward including steel content, secondary cooling water, drive pressure, soft reduction and support segments. Results show that the sulfur content of steel and support segment was the main influencing factors of the triangular area cracks. After adopting the improvement measures, the rate and level of the triangular area cracks are obviously descended.
Key words :
continuous cast slab
triangular area crack
support segment
sulfur content
macro examination
收稿日期: 1900-01-01
[1]
倪冰,刘浏,姚同路. 机械搅拌法与镁喷吹法铁水搅拌能和混匀时间的关系 [J]. , 2014, 24(3): 9-13.
[2]
卢巧婷,冯立果,贾改风. 抗硫化氢腐蚀容器钢Q345R(R-HIC)的生产实践 [J]. , 2014, 24(09): 29-32.
[3]
王鑫潮,王红娜,成国光,寇玉山,左辉,陈列. 20Cr13不锈钢热轧棒材夹杂物研究 [J]. , 2014, 25(07): 17-21.
[4]
封波,徐昊,高卫,吴六顺,董元篪. LF精炼渣低氟化研究进展 [J]. , 2014, 24(06): 1-5.
[5]
秦登平, 朱志远, 危尚好. 镁基喷吹深脱硫回硫控制分析 [J]. Journal of Materials Sciences & Technology, 2013, 23(7): 33-36.
[6]
董大西 , 王 谦, 李国栋, 高 晗, 陈良勇 , 李荣祥. 含硫易切削钢连铸坯低倍裂纹的成因及控制 [J]. Journal of Materials Sciences & Technology, 2013, 23(6): 30-33.
[7]
刘晓峰, 安昌遐 , 杜亚伟, 陈登国. VD真空精炼技术与装备的发展现状 [J]. Journal of Materials Sciences & Technology, 2013, 23(5): 7-11.
[8]
杨荣光, 王志刚. 超低硫钢精炼工艺生产实践 [J]. Journal of Materials Sciences & Technology, 2013, 23(5): 34-37.
[9]
周贺贺, 曹余良, 王攀峰, 孟令东. 低硅钢冶炼工序硅质量分数控制 [J]. Journal of Materials Sciences & Technology, 2013, 23(5): 41-43.
[10]
曹 锋, 霍吉祥. 首钢京唐1号高炉铁水含硫高的分析 [J]. Journal of Materials Sciences & Technology, 2013, 23(10): 22-25.
[11]
王阳. X80连铸板坯角部裂纹的生产实践与分析 [J]. Journal of Materials Sciences & Technology, 2012, 22(9): 47-50.
[12]
王国鹏. 太钢焦炉煤气脱硫和酸性气体制酸工艺实践 [J]. Journal of Materials Sciences & Technology, 2012, 22(5): 25-28.
[13]
陈洪智, 常运合, 张家泉 , 谢茂恩, 杨 东, 李六一. 不锈钢板坯连铸自由线收缩与辊缝研究 [J]. Journal of Materials Sciences & Technology, 2012, 22(2): 25-30.
[14]
刘颖义, 穆红旺, 张淑会. 焦炭质量预测模型的建立 [J]. Journal of Materials Sciences & Technology, 2012, 22(1): 28-31.
[15]
曾松盛,彭 伟, 周剑丰,成小军. SPHE用热轧薄板坯料边裂缺陷分析与改进 [J]. Journal of Materials Sciences & Technology, 2011, 21(8): 16-21.