GCr15钢液析缺陷控制工艺的探讨与改进
赵杰1 ,薛松2 ,席军良2
1. 北京科技大学材料学院,北京 100083;2.石家庄钢铁有限责任公司,河北 石家庄 050031
Discussion and Improvement of Eliquation Defect Control Technology in GCr15 Steel
ZHAO Jie1 ,XUE Song2 ,XI Junliang2
1.Material Shool Beijing University of Science and Technology, Beijing 100083,China;
2. Shijiazhuang Iron and Steel Co Ltd, Shijiazhuang 050031,Hebei,China
摘要 石家庄钢铁有限责任公司为进一步提高轴承钢质量,满足高端用户的需求,2006年批量生产GCr15轴承钢棒材,为控制并降低碳化物液析级别,进行了理论探讨和生产实践,取得了明显效果。
关键词 :
GCr15 ,
碳化物液析 ,
控制 ,
工艺
Abstract :In order to improve the quality of bearing steel and satisfy its requirement of users, theoretical research and production practice were carried out in Shijiazhuang Iron and Steel Co Ltd. Through controlling and reducing the carbide eliquation a batch of quality GCr15 bearing steel bars were successfully produced in 2006.
Key words :
GCr15
carbide eliquation
control
technology
收稿日期: 1900-01-01
[1]
李明阳. 钢渣处理工艺的设计思路 [J]. , 2014, 24(5): 1-4.
[2]
蒋大军,宋剑,何木光,杜斯宏. 钒钛磁铁矿烧结降低返矿率技术研究与实践 [J]. , 2014, 24(4): 39-44.
[3]
周民,陈莹卷,闵建军,马靳江,牛强. 高速线材减定径多道次孔型轧制有限元分析及工艺参数优化 [J]. , 2014, 24(3): 4-8.
[4]
钟华春,李建华,张南风. 模糊神经网络在加热炉温度控制中的应用 [J]. , 2014, 24(3): 18-20.
[5]
刘海波. 堆垛缓冷对Q550D-Z钢板组织性能的影响 [J]. , 2014, 24(3): 31-33.
[6]
郁祖达,叶林,潘永飞. 试论宝钢湛江钢铁炼钢厂工艺布局的创新设计 [J]. , 2014, 24(2): 44-47.
[7]
耿赛晓. 低碳冷轧用钢SPHC不同冶炼工艺的对比 [J]. , 2014, 24(10): 42-45.
[8]
王艳南,李宏,宋文臣,冯佳,. 熔融钒渣直接氧化提钒方法节能减排初步分析 [J]. , 2014, 24(10): 50-54.
[9]
陈子刚,马有辉. 中厚板温度场的分步解析求解方法及应用 [J]. , 2014, 24(1): 14-17.
[10]
金百刚,王军,李立勋,李超,贾东升,苏宽. 电磁制动技术在板坯连铸过程中的应用 [J]. , 2014, 24(1): 29-33.
[11]
梁启华,黄涛,宋满堂,张志海,王刚. 轴承钢退火工艺对带状组织的影响 [J]. , 2014, 24(09): 26-28.
[12]
王旭 袁守谦 李海潮. 矿渣棉生产发展现状的综述 [J]. , 2014, 24(08): 18-21.
[13]
刘志强. LF炉钢包底吹氩气体流量与配电联动的研究与应用 [J]. , 2014, 24(08): 22-25.
[14]
刘谦,郭传奇. 莱钢90t复吹转炉氧枪黏钢原因分析及预防措施 [J]. , 2014, 24(08): 30-32.
[15]
何木光. 控制钒钛磁铁烧结矿FeO含量的方法 [J]. , 2014, 25(07): 32-35.