SHI Jinhong1,CHEN Weiqing1,ZHANG Meiming2,LI Qing2,ZHENG Hongguang2
1.School of Metallurgical and Ecological Engineering,University of Science and Technology Beijing,Beijing 100083, China;2.Baosteel Stainless Steel Branch, Shanghai 200431, China
Abstract:Melting temperature of oxidation period slag and reducing slag as well as desulphurizing slag in 120 ton AOD of Baosteel Stainless Steel Branch was investigated by means of the method of halfspheroidal point temperature. The influence factors of AOD slag melting point were studied. The results show that for the AOD slag in oxidation period, the influence of basicity and MgO on slag melting point is little. The slag melting point increases with the increase of TFe in oxidation slag as TFe content range from 10% to 20%, and in addition, the slag melting point increases 140 ℃ with Cr2O3 content in the slag increases from 225% to 30%. For the final desulphurizing slag, the slag melting point increases remarkably as the slag basicity changed from 1.4 to 1.8. The slag melting point decreases observably in the range of CaF2 addition 12%~13% for desulphurizing slag of basicity 18, and in the range of CaF2 addition 95%~105% for reduction slag of basicity 1.6.
师金红1 ,陈伟庆1 ,张昧茗2 ,李青2 ,郑宏光2. AOD炉渣熔化温度的实验研究[J]. 中国冶金, 2007, 17(12): 41-41.
SHI Jinhong1,CHEN Weiqing1,ZHANG Meiming2,LI Qing2,ZHENG Hongguang2. Study on Melting Temperature of AOD Slag. China Metallurgy, 2007, 17(12): 41-41.