1.Material and Metallurgy Department, Wuhan University of Science and Technology, Wuhan 430080, Hubei, China, 2. No.1 Steelmaking Plant, Wuhan Iron and Steel Corp., Wuhan 430083, Hubei, China
Abstract：This article analyzes and discusses about thermodynamic and kinetic factors of secondary refining desulphurization. It shows briefly the technologies and methods for ladle furnace refining desulfurization through discussing about converter operating control, slag melting and forming quickly at LF, refining temperature, steelslag deoxidation, choosing proper slag system and optimizing chemical composition of ladle slag,etc.
赵中福1，2 ,赵继宇2 ，李小明2 ,王金平2. 100 t LF精炼脱硫生产实践[J]. 中国冶金, 2009, 19(4): 18-18.
ZHAO Zhongfu1,2,ZHAO Jiyu2,LI Xiaoming2,WANG Jinping2. Production Practice About Desulfurization of Steel for 100 t Ladle Furnace Refining Process. China Metallurgy, 2009, 19(4): 18-18.