Quantificational Analysis for NonCrystalline and Crystalline Solids in Blast Furnace Slag
WANG Haifeng,GUO Peimin,ZHANG Chunxia,QI Yuanhong
State Key Laboratory of Advanced Steel Processing and Products,Central Iron and Steel Research Institute,Beijing China 100081
摘要 利用X射线衍射法分析了高炉渣中的非晶态和晶态含量,高炉渣(主要成分为w(CaO)382%,w(SiO2)357%,w(Al2O3)163%,w(MgO)83%)中晶态与非晶态含量的定量比例系数为070。
关键词 :
高炉渣 ,
非晶态 ,
晶态 ,
定量分析
Abstract :The quantificational analysis for the noncrystalline and the crystalline solids in blast furnace (BF)slag was conducted with Xray diffraction method. The quantificational coefficient between the crystalline and the noncrystalline solids (the main composition of BF slag used: CaO 382%,SiO2357%,Al2O3163%,MgO 83%) is 070.
Key words :
blast furnace slag
noncrystalline
crystalline
quantificational analysis
收稿日期: 1900-01-01
引用本文:
王海风,郭培民,张春霞,齐渊洪. 高炉渣中非晶态及晶态含量的定量分析[J]. 中国冶金, 2007, 17(7): 41-41.
WANG Haifeng,GUO Peimin,ZHANG Chunxia,QI Yuanhong. Quantificational Analysis for NonCrystalline and Crystalline Solids in Blast Furnace Slag. China Metallurgy, 2007, 17(7): 41-41.
链接本文:
http://www.zgyj.ac.cn/CN/ 或 http://www.zgyj.ac.cn/CN/Y2007/V17/I7/41
[1]
张殿伟 ,赵志星,赵宝军. 首钢高炉渣与配制四组元渣的黏度研究 [J]. , 2014, 24(4): 11-15.
[2]
秦跃林,邱贵宝,白晨光,吕学伟,邓青宇. 化学法回收高炉熔渣显热的研究进展 [J]. Journal of Materials Sciences & Technology, 2011, 21(4): 1-7.
[3]
王海风,张春霞,齐渊洪. 高炉渣处理和热能回收的现状及发展方向 [J]. Journal of Materials Sciences & Technology, 2007, 17(6): 53-53.