三种球团膨胀率计算方法的比较
任伟,周明顺,李艳茹
鞍钢股份有限公司技术中心, 辽宁 鞍山 114021
Three Methods for Calculating Pellets Expanding Rate
REN Wei, ZHOU Mingshun,LI Yanru
Technical Centre, Anshan Iron and Steel Co Ltd, Anshan 114021, Liaoning, China
摘要 为研究计算方法对直径法测量球团体膨胀率的影响,对3种计算方法进行了分析和比较。研究结果表明,在球团线膨胀率(同一球团膨胀尺寸与膨胀前的直径之比)不变的情况下,随膨胀前球团直径波动范围的扩大,通过3种方法计算所得体膨胀率相差越来越大,但大小对比关系变化甚微;在膨胀前球团直径波动范围不变的情况下,随线膨胀率波动范围的扩大,在3种计算方法中,方法3和方法1取得最大最小值的次数越来越多,三者间的差异也越明显。
关键词 :
球团 ,
膨胀率 ,
计算方法
Abstract :Three methods for calculating pellets expanding rate were analyzed in order to evaluate the effect of calculation method on expanding rate. Results show that at a fixed liner expanding rate (diameter ratio between before and after expanding), the greater the diameter of pellet fluctuates is, the larger the difference among three methods for calculating expanding rate is. When the range of fluctuation is fixed and the liner expanding rate is enlarged, frequency of maximum and minimum value by method 3 and method 1 is highest and the difference among three methods is obvious.
Key words :
pellet
expanding rate
method of calculation
收稿日期: 1900-01-01
[1]
高雅巍, 李京社, 刘成松, 唐海燕. 不同类型铁矿石的低温还原粉化特征 [J]. Journal of Materials Sciences & Technology, 2013, 23(10): 1-5.
[2]
张作良, 李 强, 高 攀, 李明明, 张 伟, 邹宗树 . 高铝铁矿石球团气基还原物相状态研究 [J]. Journal of Materials Sciences & Technology, 2013, 23(10): 10-13.
[3]
王兆才, 陈双印, 储满生, 柳政根, 张健伟. 煤制气-竖炉生产直接还原铁浅析 [J]. Journal of Materials Sciences & Technology, 2013, 23(1): 20-25.
[4]
赵民革. 以科技进步为基础、创新求发展——近几年铁矿粉造块技术发展综述 [J]. Journal of Materials Sciences & Technology, 2011, 21(9): 4-13.
[5]
叶匡吾, 冯根生. 高炉炼铁合理炉料结构新概念 [J]. Journal of Materials Sciences & Technology, 2011, 21(9): 1-3.
[6]
张立国,张宗旺,任彤旭. 鞍钢球团配加白云石熔剂的研究 [J]. Journal of Materials Sciences & Technology, 2011, 21(8): 34-38.
[7]
储满生,柳政根,王兆才,吴开基,吕继平. 反应气氛和温度对热压含碳球团还原反应进程的影响 [J]. Journal of Materials Sciences & Technology, 2011, 21(4): 17-20.
[8]
赵玉潮, 曾香梅, 郑志强, 宁振, 徐毅, 莫朝文. 配加精炼渣和低价矿生产炼钢用熔剂性球团矿的试验研究 [J]. Journal of Materials Sciences & Technology, 2010, 20(9): 34-39.
[9]
刘杰,周明顺,翟立委,任伟,李金莲. 澳大利亚卡拉拉精矿造球性能的研究 [J]. Journal of Materials Sciences & Technology, 2010, 20(10): 28-31.
[10]
杨雪峰. 昆钢球团生产线提高生球成球率的研究与应用 [J]. Journal of Materials Sciences & Technology, 2010, 20(1): 30-30.
[11]
刘士友1 ,李娜2 ,郝素菊2 ,王永强2 ,蒋武锋2. 用高含碳金属化球团处理焦化废水的研究 [J]. Journal of Materials Sciences & Technology, 2009, 19(7): 42-42.
[12]
康兴东1 ,陈志英2 ,夏春才3 ,陈铁军4 ,张华丽4 ,马蕾4. 提高程潮球团质量的试验研究 [J]. Journal of Materials Sciences & Technology, 2009, 19(1): 36-36.
[13]
白仕平,张丙怀,伍成波,贾国利. 高炉瓦斯泥高效利用的实验研究 [J]. Journal of Materials Sciences & Technology, 2007, 17(6): 40-40.
[14]
叶匡吾. 坚持球团矿生产的大型化发展方向 [J]. Journal of Materials Sciences & Technology, 2007, 17(6): 1-1.
[15]
伍成波,杨辉,张丙怀,马丁. 含锌电炉粉尘处理的扩大性实验 [J]. Journal of Materials Sciences & Technology, 2007, 17(5): 52-52.