Abstract:In order to give full play to the advantages of raw material strong adaptability of the belt roasting machine and reduce the production cost of pellets, the coarse sintering powder ore was treated to a certain particle size and moisture by closed-circuit grinding process, and used in combination with magnetite concentrate as raw material for pelletizing production. The influence of green ball and roasted ball on the pellet production line of belt roasting machine was investigated through industrial test. The test results show that when the proportion of MAC fines is less than 30%, it can be ensured that the proportion of fine grinding particle with size less than 0.074 mm (200 mesh) is more than 90%, and the water content of filter cake is less than 9%, which can meet the raw material requirements of pellet production. The drop times and compressive strength of green ball are enhanced with the increasing of grinded-fine ratio. The addition of grinded-fine can reduce the amount of bentonite and improve the iron grade of pellets. The addition of grinded-fine will reduce the compressive strength of roasted ball, but has no obvious effect on the reduction degree and low temperature reduction pulverization rate. In summary, an ideal ore blending scheme is that SFCJ powder, SSFS powder and MAC powder are mixed at the ratio of 4∶3∶3 and filtered, and then the grinded-fine obtained is added to the pellet raw materials at the ratio of 40%,which can reduce the production cost of pellet.
姜涛. 铁矿造块学[M]. 长沙:中南大学出版社,2016.(JIANG T. Principle and Technology of Agglomeration of Iron Ores[M]. Changsha:Central South University Press,2016.)
[2]
许满兴,张玉兰. 新世纪我国球团矿生产技术现状及发展趋势[J]. 烧结球团,2017,42(2):25.(XU M X,ZHANG Y L. Analysis of pellet technology and production of China in 21 st century[J]. Sintering and Pelletizing,2017,42(2):25.)
[3]
张福明. 炼铁系统低碳技术发展前景与途径[J]. 钢铁,2022,57(9):11.(ZHANG F M. Development prospects and methods on low-carbon technology in ironmaking system[J]. Iron and Steel,2022,57(9):11.)
[4]
王海风,裴元东,张春霞,等. 中国钢铁工业烧结/球团工序绿色发展工程科技战略及对策[J]. 钢铁,2016,51(1):1.(WANG H F,PEI Y D,ZHANG C X,et al. Green development of sintering/pellet procedure in China iron and steel industry[J]. Iron and Steel,2016,51(1):1.)
[5]
张福明. 首钢绿色低碳炼铁技术的发展与展望[J]. 钢铁,2020,55(8):11.(ZHANG F M. Development and prospect of green and low carbon ironmaking technologies in Shougang[J]. Iron and Steel,2020,55(8):11.)
[6]
张琦. 中国钢铁行业碳达峰碳中和时间表与路线图[J]. 钢铁,2023,58(9):59.(ZHANG Q. Roadmap and timetable for achieving carbon peak and carbon neutrality of China's iron and steel industry[J]. Iron and Steel,2023,58(9):59.)
[7]
苍大强. 钢铁工业“碳达峰”“碳中和”及低碳技术的误区及现实路径[J]. 中国冶金,2021,31(9):3.(CANG D Q. Misunderstandings and realistic path of "carbon peak" "carbon neutrality" and low carbon technologies in iron and steel industry[J]. China Metallurgy,2021,31(9):3.)
[8]
胡长松. 首钢高炉新炉料结构下球团技术的探索与应用[J]. 中国冶金,2021,31(6):54.(HU C S. Exploration and application of pelletizing technology under new burden structure of blast furnace in Shougang[J]. China Metallurgy,2021,31(6):54.)
[9]
彭道胜. 细磨卡粉制备熔剂性球团的试验研究[J].烧结球团,2021,46(4):50.(PENG D S. Experimental research on preparation of fluxed pellets from fine grinding Carajas powder[J]. Sintering and Pelletizing,2021,46(4):50.)
[10]
赵连达,刘迎立,苏鸿,等. 添加赤铁矿对碱性球团性能的影响[J]. 中国冶金,2021,31(3):11.(ZHAO L D,LIU Y L,SU H,et al. Effect of adding hematite on properties of alkaline pellets[J]. China Metallurgy,2021,31(3):11.)
[11]
范晓慧. 烧结球团厂设计原理[M]. 长沙:中南大学出版社,2016.(FAN X H. Principle of design for sintering and pelletizing plant of iron ores[M]. Changsha:Central South University Press,2016.)
[12]
智谦,韩志国,易毅辉,等. 包钢624 m2大型带式球团焙烧机设计创新与应用[J]. 中国冶金,2017,27(4):61.(ZHI Q,HAN Z G,YI Y H,et al. Design innovation and application of 624 m2 travelling grate machine at Baogang[J]. China Metallurgy,2017,27(4):61.)
[13]
李新宇,张建良,刘依然,等. 带式焙烧机生产磁-赤型球团矿焙烧试验研究[J]. 烧结球团,2015,40(4):28.(LI X Y,ZHANG J L,LIU Y R,et al. Experimental research on roasting and production of magnetite-hematite type pellets with traveling grate[J]. Sintering and Pelletizing,2015,40(4):28.)
[14]
范建军. 高压辊磨预处理对超细粒度磁铁精矿粉球团性能的影响[J]. 钢铁,2012,47(9):19.(FAN J J. Effect of high pressure roll grinding on pellet property of super-fine magnetite concentrate[J]. Iron and Steel,2012,47(9):19.)
[15]
范晓慧,袁晓丽,李光辉,等. 铁精矿粒度对球团强度的影响[J]. 中国有色金属学报,2006,16(11):8.(FAN X H,YUAN X L,LI G H,et al. Effect of particle size distribution of concentrate on palletizing quality[J]. The Chinses Journal of Nonferrous Metals,2006,16(11):8.)
马丽,青格勒,田筠清,等. 球团配加细磨麦克粉的试验研究[J]. 烧结球团,2019,44(2):39.(MA L,QING G L,TIAN J Q,et al. Experimental study on pelletizing proportioned with grinded MAC fines[J]. Sintering and Pelletizing,2019,44(2):39.)
[18]
刘桐,张俊杰,贾来辉,等. 高配比褐铁矿在线球磨矿在球团生产中的应用[J]. 烧结球团,2023,48(4):52.(LIU T,ZHANG J J,JIA L H,et al. Application of online ball grinding of high proportion limonite in pellet production[J]. Sintering and Pelletizing,2023,48(4):52.)
[19]
黄伟青,张旭孝,刘燕霞,等. 褐铁矿在烧结中的高效使用技术[J]. 钢铁研究学报,2016,28(7):13.(HUANG W Q,ZHANG X X,LIU Y X,et al. High effective utilization technology of limonite in sintering[J]. Journal of Iron and Steel Research,2016,28(7):13.)
[20]
侯健,白晨光,琥玫珑,等. 南非PMC精粉与两种典型褐铁矿的配矿优化[J]. 钢铁,2023,58(6):45.(HOU J,BAI C G,HU M L,et al. Optimization on ore-blending of PMC concentrate and two typical limonite ore[J]. Iron and Steel,2023,58(6):45.)
[21]
严照照,卢建光,吕庆,等. MgO对生球质量和球团矿抗压强度的影响[J]. 钢铁钒钛,2017,38(6):98.(YAN Z Z,LU J G,LÜ Q,et al. Impact of magnesium oxide on the green ball quality and cruslring strength of pellets[J]. Iron Steel Vanadium Titanium,2017,38(6):98.)
[22]
李光辉,彭志伟,杨雪峰,等. 提高昆钢生球质量及成品率的研究与实践[J]. 钢铁,2007,42(10):20.(LI G H,PENG Z W,YANG X F,et al. Research and practice of improving quality and yield of pellets at Kunsteel[J]. Iron and Steel,2007,42(10):20.)
[23]
廖军平,陈昭尧. SG带式焙烧机镁质球团矿的生产应用[J]. 中国冶金,2021,31(10):51.(LIAO J P,CHEN Z Y. Production and application of SG belt roaster magnesium pellet[J]. China Metallurgy,2021,31(10):51.)
[24]
朱德庆,黄伟群,杨聪聪,等. 铁矿球团技术进展[J]. 烧结球团,2017,42(3):42.(ZHU D Q,HUANG W Q,YANG C C,et al. Technical progress in iron ore pelletization[J]. Sintering and Pelletizing,2017,42(3):42.)
[25]
张淑会,王宝勇,兰臣臣,等. 球团矿化学成分控制现状及展望[J]. 钢铁,2020,55(8):1.(ZHANG S H,WANG B Y,LAN C C,et al. Prospects and present status of pellets chemical composition control[J]. Iron and Steel,2020,55(8):1.)
[26]
余海钊,廖继勇,范晓慧. 带式焙烧机球团技术的应用及研究进展[J]. 烧结球团,2020,45(4):47.(YU H Z,LIAO J Y,FAN X H. Application and research progress of pelletizing technology of belt roaster[J]. Sintering and Pelletizing,2020,45(4):47.)
[27]
张福明,张卫华,青格勒,等. 大型带式焙烧机球团技术装备设计与应用[J]. 烧结球团,2021,46(1):66.(ZHANG F M,ZHANG W H,QING G L,et al. Design and application on pelletizing technologies and equipments in large-scale belt type roasting machine[J]. Sintering and Pelletizing,2021,46(1):66.)
[28]
姜涛,何国强,李光辉,等. 脉石成分对铁矿球团还原膨胀性能的影响[J]. 钢铁,2007,42(5):7.(JIANG T,HE G Q,LI G H,et al. Effect of Gangue composition on reduction swelling of iron ore pellets[J]. Iron and Steel,2007,42(5):7.)
[29]
白明华,符远翔. 球团矿恒温和升温直接还原膨胀行为试验[J]. 钢铁,2015,50(6):35.(BAI M H,FU Y X. Swelling behavior of iron ore pellets for direct reduction in isothermal and temperature-rising conditions[J]. Iron and Steel,2015,50(6):35.)
[30]
皮晓东,孙权,罗果萍,等. 球团矿还原膨胀机理研究概况[J]. 烧结球团,2017,42(4):28.(PI X D,SUN Q,LUO G P,et al. Research review on reduction expansion mechanism of pellets[J]. Sintering and Pelletizing,2017,42(4):28.)