Study of press of cubic iron oxide during the straightening stage for plates
SUN Bing-hong1,2,WANG Ga1,XU Shao-pu1,FU Dai-li1,LUO Hong-tao1,LI Yang1
1. Steelmaking and Rolling Plant, Nanyang Hanye Special Steel Co., Ltd., Nanyang 474500, Henan, China 2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
Abstract:Through statistical analysis and comparison experiment, the plate straightening process, the possibility of press of cubic iron oxide under working roller pressure into the steel plate surface in the powerful straightening machine and the defect caused on the plate surfacewere proved. And the morphology and characteristics of defects were summarized; the process and reason of the press of iron oxide were analyzed. It points out that the generation of the cubic ferric oxide, iron oxide under external bending stress cracking and accumulation, and the perpendicular pressure to the plate surface during the straightening process were the three necessary conditions; it also points out several key technology points which affect the press of iron oxide during plate straightening and how to prevent or reduce the defect of press of iron oxide during straightening process.
孙炳红 ,王嘎,许少普,符代砺,罗红涛,李扬. 中厚板矫直环节三次氧化铁皮压入的研究[J]. 中国冶金, 2015, 25(04): 56-59.
SUN Bing-hong,,WANG Ga,XU Shao-pu,FU Dai-li,LUO Hong-tao,LI Yang. Study of press of cubic iron oxide during the straightening stage for plates. China Metallurgy, 2015, 25(04): 56-59.