1. Metallurgical and Ecological Engineering School, University of Science and Technology Beijing, Beijing 100083，China 2. Iron and Steel Institute, Nanyang Hanye Special Iron and Steel Co．，Ltd．， Nanyang 474500， Henan, China
Abstract：In the roller hearth heat treatment furnace production, the cause and formation of bottom roller nodulation were analyzed, the mechanism of heat-treated plate roller printing was cleared, high-temperature fiber composite to solve practical plate roll printing problem was proposed. It has been concluded that the hardness is less than the hardness of steel plates when the high-temperature fiber surface is not oxidized, not sintered,not nodulated, and under high temperature. The effective solution to the plate surface quality problems was raised, and the abrasion resistance is good, structural strength is high, anxious cold performance is good, and it is able to adapt to roller hearth furnace out of the discharge end of the opening for the production model.
唐郑磊 ，陆岳璋，许少普，杨阳. 热处理中厚板辊印分析及解决实践[J]. 中国冶金, 2015, 25(05): 36-39.
TANG Zheng-lei,,LU Yue-zhang,XU Shao-pu,,YANG Yang. Analysis and solving practice of heat treatment of plate roll printing. China Metallurgy, 2015, 25(05): 36-39.
2015, Vol. 25 