Effect of reheating temperature and continuous annealing temperature on product quality of IF steel
WANG Lin1, YU Yang1, WANG Chang1, ZHANG Dong1, WANG Ming-zhe2, JIAO Hui-li2
1. Research Institute of Technology, Shougang Group Co., Ltd., Beijing 100043, China; 2. Manufacturing Department, Beijing Shougang Co., Ltd., Qian'an 064404, Hebei, China
Abstract:Taking deep drawing steel DC06 as the research object, the microstructure, precipitates and mechanical properties of continuous annealed IF steel products were simulated and analyzed under different reheating temperatures (1 150-1 250 ℃) and different continuous annealing temperatures (760-840 ℃) in laboratory. The results showed that lowering the reheating temperature of continuous casting slab could coarsen the grains and precipitates, improve the strain hardening index and elongation after fracture, and reduce the strength of the final products. For the certain mechanical property requirement of the final product, a lower continuous annealing temperature could be matched to achieve cost reduction and efficiency increase.
王林, 于洋, 王畅, 张栋, 王明哲, 焦会立. IF钢加热和连退温度对成品质量影响分析[J]. 中国冶金, 2020, 30(8): 64-68.
WANG Lin, YU Yang, WANG Chang, ZHANG Dong, WANG Ming-zhe, JIAO Hui-li. Effect of reheating temperature and continuous annealing temperature on product quality of IF steel[J]. China Metallurgy, 2020, 30(8): 64-68.