Effect of air quenching process on granulation of AOD stainless steel slag
ZOU Jing-jing1,2, MA Guo-jun1,2, YAO Wang-long1,2, ZHANG Xiang1,2
1. Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China; 2. Hubei Provincial Key Laboratory of New Processes of Ironmaking and Steelmaking, Wuhan University of Science and Technology, Wuhan 430081, Hubei, China
Abstract:To improve the stability of stainless steel argon oxygen decarburization(AOD) slag, the AOD slag was granulated by air quenching, and the influences of slag basicity, modifier, slag temperature, flow velocity, and injection angle on the slag granulation result were studied. The results showed that with the slag basicity decreasing, the mean diameter firstly decreased to the minimum mean diameter of 4.31 mm at the basicity of 1.8 and then gradually increased. After the adjunction of B2O3, with the decrease of basicity the change trend of the mean diameter of the slag was the same with before modification, but the mean diameter overall decreased. With the temperature of the slag increasing, the mean diameter of the slag increased. With the flow velocity increasing and the injection angle decreasing, the mean diameter of the slag gradually decreased to the minimum mean diameter of 3.67 mm at the flow velocity of 21.5 m/s; the minimum mean diameter of the slag of 4.28 mm was obtained at the injection angle of 25°.
邹晶晶, 马国军, 姚旺龙, 张翔. 风淬工艺对粒化不锈钢氩氧脱碳炉渣的影响[J]. 中国冶金, 2021, 31(7): 63-69.
ZOU Jing-jing, MA Guo-jun, YAO Wang-long, ZHANG Xiang. Effect of air quenching process on granulation of AOD stainless steel slag[J]. China Metallurgy, 2021, 31(7): 63-69.
SHEN H.Physicochemical and mineralogical properties of stainless steel slags oriented to metal recovery[J].Resource Conservation and Recycling,2004,40(3):245.
Hannemann F,Bradfield M,Mahdi M.Impact of air granulation on the ferrochrome value chain in metallurgical smelter complexes [J].The Southern African Institute of Mining and Metallurgy,2018,118:625.
[11]
Lindvall M,Lai Chi So L,Mahdi M.Stabilization of stainless steel slag via air granulation[J].Journal of Sustainable Metallurgy,2019(5):157.
[12]
Kriskova L,Pontikes Y,Pandelaers L,et al.Effect of high cooling rates on the mineralogy and hydraulic properties of stainless steel slags[J].Metallurgical and Materials Transactions B,2013,44(5):1173.
[13]
Mills K,Keene B. Physical properties of BOS slags[J].International Materials Reviews,1987,32(1):1.
[14]
Hanao M,Tanaka T,Kawamoto M,et al.Evaluation of surface tension of molten slag in multi-component systems[J]. ISIJ International,2007,47(7):935.
[15]
林天成.含铬转炉渣物化性质及流变特性的研究[D].重庆:重庆大学,2016.
[16]
WANG W,YAN X,ZHOU L,et al.Influences of basicity and Li2O on the properties of fluorine-free mold flux for the casting of medium carbon steels[J].Metallurgical and Materials Transactions B,2016,47(2):963.
[17]
黄希祜.钢铁冶金原理[M].北京:冶金工业出版社,2013.
[18]
LIU C,KANG Y,ZHANG Y,et al.Granulation effect analysis of gas quenching blast furnace slag with different basicities[J].Coatings,2020,10(4):372.
ZHANG L,WANG W,XIE S,et al.Effect of basicity and B2O3 on the viscosity and structure of fluorine-free mold flux[J].Journal of Non-Crystalline Solids,2017,460:113.
[22]
刘跃.高炉熔渣粒化过程熔滴凝固特性研究[D].唐山:华北理工大学,2019.
[23]
孙士纯.转炉熔融渣的风淬[J].炼钢,1986(1):72.
[24]
TONG L,ZHANG P,YIN S.Experimental study on factors that influence the diameter of dry granulated particles[J].Journal of Thermal Science,2016,25(6):571.