硅砖中裂纹的成因及其分析
王禄
(山东工业职业学院冶金学院,山东 淄博 256414)
Formation and Analysis of Crack in Silica Brick
WANG Lu
(Department of Metallurgy, Shandong Vocational College of Industry, Zibo 256414, Shandong,China)
摘要 制品受到热冲击后内部会出现热应力,当热应力过大时制品中会产生裂纹。硅砖中裂纹包括表面裂纹和层裂。表面裂纹又分为横向裂纹、竖向裂纹和网状裂纹。通常层裂和竖向裂纹是机压所致,横向裂纹和网状裂纹是烧成造成的。影响裂纹生成的主要因素是烧成和机压,但与生产过程有关的其它因素的作用也不容忽视。
关键词 :
硅砖 ,
裂纹 ,
烧成 ,
成型
Abstract :If product suffers heat concussion, it will appear heat stress. If heat stress is enough stronger, the product will produce crack. The crack occured in silica brick generally includes surface crack and layer crack. Surface crack includes horizontal, vertical and reticulate crack. Usually, layer and vertical crack are caused by moulding, and horizontal and reticulate crack are caused by sintering. The main influence factors of crack formation are sintering and moulding, but the other factors relate to producing crack are not to be neglected.
Key words :
silica brick
crack
sintering
moulding
收稿日期: 1900-01-01
[1]
李金波, 路殿华, 李建文. 铸坯皮下裂纹的演变规律研究 [J]. Journal of Materials Sciences & Technology, 2013, 23(9): 26-30.
[2]
董大西 , 王 谦, 李国栋, 高 晗, 陈良勇 , 李荣祥. 含硫易切削钢连铸坯低倍裂纹的成因及控制 [J]. Journal of Materials Sciences & Technology, 2013, 23(6): 30-33.
[3]
白瑞国, 张俊粉, 田海平, 张兴利, 田鹏. 热轧卷板表面“翘皮”的研究 [J]. Journal of Materials Sciences & Technology, 2013, 23(3): 36-39.
[4]
赵圣功. 叉车用门架槽钢Q420C质量控制与改进 [J]. Journal of Materials Sciences & Technology, 2013, 23(11): 27-31.
[5]
王阳. X80连铸板坯角部裂纹的生产实践与分析 [J]. Journal of Materials Sciences & Technology, 2012, 22(9): 47-50.
[6]
曾松盛, 彭明耀, 王仕华, 周峰, 王磊. 热轧板带中间坯料孔洞缺陷成因分析 [J]. Journal of Materials Sciences & Technology, 2012, 22(5): 38-41.
[7]
林晏民, 欧阳民, 廖美华, 姚铁梅. 保护渣高温特性对板坯表面裂纹影响的研究 [J]. Journal of Materials Sciences & Technology, 2011, 21(8): 26-29.
[8]
吕亚,王新志,李文山,刘磊,胡锐,张书铭. 超宽板坯表面纵裂纹的原因分析及预防措施 [J]. Journal of Materials Sciences & Technology, 2011, 21(6): 19-22.
[9]
蔡可森, 缪春锋, 耿建林, 李海军, 张炯明. 宽厚板中碳合金钢铸坯中间裂纹的控制策略研究 [J]. Journal of Materials Sciences & Technology, 2011, 21(5): 36-39.
[10]
兰亮云,邱春林,赵德文,高秀华,杜林秀. 冷却工艺对低焊接裂纹敏感性钢组织的影响 [J]. Journal of Materials Sciences & Technology, 2011, 21(2): 29-33.
[11]
孙彦辉1 ,赵长亮1 ,蔡开科1 ,杨素波2 ,陈永3 ,李桂军3 ,顾武安3. 连铸板坯表层网状裂纹的成因研究 [J]. Journal of Materials Sciences & Technology, 2008, 18(4): 15-15.
[12]
帅习元1 ,陈洪伟1 ,周勇1 ,魏路敏2. 冷镦钢冷镦开裂原因及其改进措施 [J]. Journal of Materials Sciences & Technology, 2008, 18(4): 33-33.
[13]
吕铭,王健,郭伟达,刘平,费燕,黄优明. 20CrMnTiH钢顶锻裂纹分析与控制措施 [J]. Journal of Materials Sciences & Technology, 2008, 18(2): 19-19.
[14]
赵新凯, 刘西峰,韩爱丽. 冷轧低碳铝镇静钢表面裂纹分析 [J]. Journal of Materials Sciences & Technology, 2008, 18(12): 22-22.
[15]
魏励,杨海滨. 连铸含铌钢板坯表面横裂纹原因分析和措施 [J]. Journal of Materials Sciences & Technology, 2008, 18(12): 17-17.