Experimental study of roll composite for low-alloy ultra-heavy steel plate
WANG Xiao-yong1, WANG Hua-peng2, JIA Xiao-lin2, ZOU Yang1, PIAO Xue-feng2
1. Research Institute of Technology, Shougang Group Co., Ltd., Beijing 100043,China; 2. Heavy Plate Department, Shougang Jingtang United Iron and Steel Co., Ltd., Tangshan 063210, Hebei, China
Abstract:In order to meet the market demand of low-alloy steel plate with large single weight and ultra-heavy specifications, the experimental study of ultra-heavy steel plate produced by composite continuous casting slab was carried out by the rolling composite process. Ultra-heavy steel plates were obtained through rolling from composite slab. The comprehensive test and analysis show that the interface bonding of ultra-heavy steel plate produced by rolling composite process is good, and metallurgical bonding at atomic level is achieved with the sufficient recrystallization of grain at the bonding interface. The z-direction tensile properties meet the requirements of Z35, but the local reduction of area is low due to the existence of band-distributed oxides at the bonding interface microregion.
王小勇, 王华鹏, 贾啸林, 邹扬, 朴学峰. 低合金特厚钢板轧制复合试验[J]. 中国冶金, 2022, 32(7): 98-102.
WANG Xiao-yong, WANG Hua-peng, JIA Xiao-lin, ZOU Yang, PIAO Xue-feng. Experimental study of roll composite for low-alloy ultra-heavy steel plate[J]. China Metallurgy, 2022, 32(7): 98-102.