Reason analysis and control of typical steel leakage of thin slab continuous casting production of SS400 steel
JI De-jing1,LI Chun-yang2,SU Jia-nan2
1.Jilin Electronic Information Professional Technology Institute, Jilin 132021, Jilin, China 2.Jilin Ferroalloy Company Limited of Sinosteel, Jilin 132021, Jilin, China)
Abstract:Based on the production of SS400 steel by continuous casting slab in a certain factory, the typical steel leakage phenomenon was analyzed through chemical composition analysis, continuous casting parameters analysis, the FDA curve analysis, steel image analysis and the real reason for the leakage of steel was found. It was mainly caused by the leakage of steel slag, and effective measures were taken to prevent similar production accidents in the future. Measures included: to ensure the overheat temperature of the molten steel in the tundish between 15 to 35℃ in the steelmaking section; in accordance with the relevant provisions of 0.1 m/min every time when reduce speed to ensure the smooth production and improve the continuous casting machine operation efficiency.
收稿日期: 2014-05-20
出版日期: 2015-01-20
通讯作者:
季德静
E-mail: jidejing8341@126.com
引用本文:
季德静,李春阳,苏家男. SS400钢薄板坯连铸生产典型漏钢原因分析和控制[J]. 中国冶金, 2015, 25(01): 41-44.
JI De-jing,LI Chun-yang,SU Jia-nan. Reason analysis and control of typical steel leakage of thin slab continuous casting production of SS400 steel. China Metallurgy, 2015, 25(01): 41-44.