Effect of austenizing temperature on microstructure and mechanical properties of 40CrNiMo steel |
XIONG Guo-yuan, LIU Li-hua, ZHU Wen-tao |
CITIC Dicastal Co., Ltd., Qinhuangdao 066011, Hebei, China |
|
|
Abstract Effect of austenizing temperature on hardenability, microstructure of 40CrNiMo steel after quenching at a cooling rate of 0.7 ℃/s and microstructure and mechanical properties of 40CrNiMo steel after tempering was studied. Results showed that with increasing temperature from 800 to 1 000 ℃, the hardenability was increased gradually, especially when the temperature exceeded 950 ℃. When the austenitizing temperature was 800 ℃, there was some ferrite in the microstructure, resulting in lower hardness but higher toughness. When the austenitizing temperature was 900 ℃, the specimen possessed the highest strength but the ductility was lower. The fracture mechanism was also changed with increasing temperature, especially for impact specimens. All tensile specimens exhibited ductile fracture with dimples in the fracture surface. However, impact specimens changed from dimple fracture to cleavage or quasi-cleavage fracture, with more typical river pattern in the fracture surface when the austenitizing temperature exceeded 900 ℃.
|
Received: 29 March 2021
|
|
|
|
[1] |
王敬忠,李科元,刘阿娇,等. 40CrNiMo钢国内外研究现状[J]. 钢铁,2018,53(5):1.
|
[2] |
张彦文,吴立新,王志奋,等. 包覆机主轴腐蚀疲劳断裂分析[J]. 中国冶金,2016,26(1):47.
|
[3] |
李占鑫,张胜超. 淬火介质SST103在调质钢及轴承钢热处理中的应用[J]. 物理测试,2008(4):15.
|
[4] |
陈立奇,段世浩,钟红春. 40CrNiMoE钢锻件的热处理与力学性能[J]. 金属热处理,2011,36(7):77.
|
[5] |
李忠波,唐郑磊,许少普,等. 水电用SX610CF特厚钢板的研发[J]. 轧钢,2019,36(4):19.
|
[6] |
Hwang B,Suh D W,Kim S J. Austenitizing temperature and hardenability of low-carbon boron steels[J]. Scripta Materialia,2011,64(12):11.
|
[7] |
张晓东,夏佃秀,王守仁,等. 奥氏体化温度对51CrV4钢淬火组织和性能的影响[J]. 钢铁,2019,54(3):76.
|
[8] |
姜在伟,张舒展,李艳梅,等. 奥氏体化温度对SA738Gr.B核电钢的显微结构及回火后性能的影响[J]. 材料与冶金学报,2020,43(3):227.
|
[9] |
孙东云,陈晨,张福成,等. 奥氏体化温度对V微合金中碳钢淬透性与力学性能的影响[J]. 燕山大学学报,2019,19(3):189.
|
[10] |
陈晨,杨志南,张洋,等. 大功率风电偏航轴承套圈用钢及其模拟热处理工艺[J]. 机械工程学报,2015,51(14):29.
|
[11] |
Siebert C A,Doane D V,Breen D H. The Hardenability of Steels [M]. Metals Park,Ohio:American Society for Metals,1977.
|
[12] |
Totten G E. Steel Heat Treatment:Metallurgy and Technologies [M]. New York:CRC Press,2006.
|
[13] |
张玉妥,边书,韩维新. 25CrMo钢端淬试验改进与淬透性分析[J]. 材料热处理学报,2015,36(2):162.
|
[14] |
Grossman M A. Hardenability calculated from chemical composition [J]. Transactions of the Metallurgical Society of AIME,1942,150:227.
|
[15] |
叶宏. 金属热处理原理与工艺[M]. 北京:化学工业出版社,2011.
|
[16] |
陈豪,周天鹏,陈泽军,等. 回火温度对30Cr15Mo1 N微观组织和力学性能影响[J]. 钢铁,2019,54(5):60.
|
[17] |
任勇强,谢振家,张宏伟,等. 前躯体组织对C-Mn-Si钢组织特征及力学行为的影响[J]. 金属学报,2013,49(12):1558.
|
[18] |
左越,周世同,李昭东,等. V和Si对珠光体车轮钢显微组织和力学性能的影响规律[J]. 材料研究导报,2016,30(6):401.
|
[19] |
邹伟龙,王毛球,时捷,等. 热处理对25CrNi3MoV钢组织与力学性能的影响[J]. 金属热处理,2008(7):69.
|
[20] |
周成,赵坦,朱隆浩,等. 淬火温度对620 MPa级海洋工程用钢组织及性能的影响[J]. 材料热处理学报,2019,40(1):112.
|
[21] |
钟群鹏,赵子华. 断口学[M]. 北京:高等教育出版社,2006.
|
[22] |
廖乾初,孙福玉,蓝芬兰. 准解理断裂的本质[J]. 金属学报,1979,15(2):259.
|
[23] |
蒋元凯,李传维,王淑侠,等. 显微组织对SA508 Gr.3钢断裂方式的影响[J]. 材料热处理学报,2019,40(4):98.
|
[24] |
管彦朋,李亚江,王娟. 1 200 MPa高强耐磨钢焊缝显微组织及冲击韧性的研究[J]. 机械制造文摘(焊接分册),2015(2):5.
|
|
|
|