Abstract:White etching crack (WEC) is a failure mode different from the classical rolling contact fatigue (RCF) and one of the most concerned failure modes because it usually results in premature failures. The difference between WEC failure and classical RCF is briefly introduced, then the effects of additional loads, bearing materials and heat treatment, surface coating on WEC failure lifetime of bearings, and the influence of steel cleanliness on WEC and RCF lifetimes of bearings are investigated with rig tests. It is proved that the additional loads are necessary to WEC formation, and improving steel cleanliness is only effective to prolong classical RCF lifetime but not effective to WEC failure lifetime of bearings.
Zwirlein O, Schlicht H. Rolling contact fatigue mechanisms-accelerated testing versus field performance[C]//Rolling Contact Fatigue Testing of Bearing Steels. Phoenix: ASTM International, 1982:358.
[2]
Kyozaburo Furumura, Yasuo Murakami, Tsutomu Abe. Development of long life bearing steel for full film lubrication and for poor and contaminated lubrication[J]. Motion and Control, 1996(1):30.
[3]
Jörg Loos, Andreas Mangold, Toni Blaβ, et al. Bearing currents as WEC-trigger in wind turbines[C]//4th Conference for Wind Power Drives 2019. Aachen: Center for Wind Power Drives of the RWTH Aachen, 2019:1.
[4]
Bhadeshia H K D H. Steels for bearings[J]. Progress in Materials Science, 2012, 57:268.
[5]
Toni Blass, Werner Trojahn, Daniel Merk. Influence of material and heat treatment on the formation of WECs on test rig FE8[C]//Symposium on Advances in Steel Technologies for Rolling Bearings. Orlando: ASTM International, 2016:1.
[6]
Evans M H. White structure flaking (WSF) in wind turbine gearbox bearings: effects of ′butterflies′ and white etching cracks (WECs)[J]. Materials Science and Technology, 2012, 28(1):3.
[7]
Evans M H. An updated review: White etching cracks (WECs) and axial cracks in wind turbine gearbox bearings[J]. Materials Science and Technology, 2016, 32(11):1133.
[8]
Joerg Loos, Toni Blass, Joerg Franke, et al. Influences on generation of white etching crack networks in rolling bearings[J]. Journal of Mechanics Engineering and Automation, 2016(6):85.
[9]
Blass T, Xu X, Wunder K, et al. Influence of steel cleanliness on rolling contact fatigue and white etching crack formation[C]//12th International Symposium on Rolling Bearing Steels Progress in Bearing Steel, Metallurgical Testing and Quality Assurance. Denver: ASTM International, 2019:1.
[10]
Blass T, Trojahn W, Merk D. Influence of material and heat treatment on the formation of WECs on test rig FE8[C]//Advances in Steel Technologies for Rolling Bearings. Orlando: ASTM International, 2017:129.
[11]
Joerg Loos, Iris Bergmann, Matthias Goss. Influence of currents from electrostatic charges on WEC formation in rolling bearings[J]. Tribology Transactions, 2016, 59(5):865.
[12]
Loos J, Wehner H, Smolenski M, et al. Factors increasing the risk of WEC-formation in large-size bearings with full fluid film lubrication[C]//International Bearing Conference. Hannover: Bearing World, 2016:1.
[13]
Dinkel M, Trojahn W. Influence of sulfur inclusion content on rolling contact fatigue life[C]//Advances in Steel Technologies for Rolling Bearings. Toronto: ASTM International, 2014:1.
[14]
Schaeffler Group Industrial. FAG Rolling Bearing Catalogue[M]. Schweinfurt: Schaeffler Technologies GmBH and Co. KG, 1952, 1966, 1976, 1989, 1994, 2008.
[15]
Boehm K, Schlicht H, Zwirlein O, et al. Nonmetallic inclusions and rolling contact fatigue[C]//Bearing Steels: The Rating of Nonmetallic Inclusion. Boston: ASTM International, 1975:96.
[16]
Evans M H, Richardson A D,Wang L, et al. Confirming subsurface initiation at non-metallic inclusions as one mechanism for white etching crack (WEC) formation[J]. Tribology International, 2014, 75:87.
[17]
Richardson A D, Evans M H, Wang L, et al. The evolution of white etching cracks (WECs) in rolling contact fatigue-tested 100Cr6 steel[J]. Tribology Letters, 2018, 66:6.
[18]
Vegter R H, Slycke J T. The role of hydrogen on rolling contact fatigue response of rolling element bearing[J]. Journal of ASTM International, 2009, 7(2):1.
[19]
Richardson A D, Evans M H, Wang L, et al. Thermal desorption analysis of hydrogen in non-hydrogen-charged rolling contact fatigue-tested 100Cr6 steel[J]. Tribology Letters, 2018, 66(4):1.
[20]
Bhadeshia H K D H, Solano-Alvarez W. Critical assessment 13: Elimination of white etching matter in bearing steels[J]. Materials Science and Technology, 2015, 31(9):1011.