铁水包脱磷工艺优化与工业试验

doi:10.13228/j.boyuan.issn1006-9356.20230571

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract With the gradual reduction of high-quality minerals, the use of low-quality iron ore aggravates the dephosphorization task. How to achieve efficient and stable dephosphorization of hot metal pretreatment is a common concern of steelmaking technology researchers. The dephosphorization rate, material consumption and slag composition of iron ladle dephosphorization process in a stainless steel plant were analyzed by industrial data analysis, X-ray fluorescence analysis and direct reading spectrograph analysis. Combined with FactSage thermodynamic calculation, orthogonal test, slag mineral phase and composition analysis, the oxygen supply and slagging process of hot metal was optimized, and the process test was compared. The results show that before the process optimization, the dephosphorization rate was low and unstable, the material consumption was too much, the slag fluidity was poor, and the basicity was low. By increasing the oxygen flow rate and adjusting the addition system of slag materials, the melting point of the slag and the content of unmelted lime decrease after optimization, and more Ca₂SiO₄(C₂S) phase is formed in the slag, which is beneficial to the formation of phosphorus-rich phase. The average dephosphorization rate of the end-point dephosphorization slag is 93.2 %, which is 5.7 percentage points higher than that before optimization, the phosphorus distribution ratio of slag (L_P) increases, the average lg L_P is 4.11, which is 23% higher than that before optimization. After the process optimization, the lime consumption per ton of iron is decreased by 4.37 kg, the oxide scale consumption per ton of iron is decreased by 5.12 kg, the slagging agent consumption per ton of iron is decreased by 0.54 kg, the oxygen consumption per ton of iron is increased by 0.73 m³, and the overall consumption cost of slag materials is decreased. It is in line with efficient, stable, green and low-carbon production, which is of great significance for steel plants to enhance their product competitiveness.

Key words： iron ladle dephosphorization process optimization industrial test phase of slag material consumption

Received: 19 September 2023

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	FENG Menglong
	LIN Lu
	YAO Tonglu
	LI Xiangchen
	HE Sai

Cite this article:

FENG Menglong,LIN Lu,YAO Tonglu等. Process optimization and industrial test of iron ladle dephosphorization[J]. China Metallurgy, 2024, 34(2): 108-116.

URL:

http://www.zgyj.ac.cn/EN/10.13228/j.boyuan.issn1006-9356.20230571 OR http://www.zgyj.ac.cn/EN/Y2024/V34/I2/108

[1]	LIN L,ZENG J Q. Consideration of green intelligent steel processes and narrow window stability control technology on steel quality[J]. International Journal of Minerals,Metallurgy and Materials,2021,28(8):1264.
[2]	范越,李胜利,艾新港,等. 窄窗口控制及大数据在直轧的应用现状与展望[J]. 中国冶金,2018,28(9):8.(FAN Y,LI S L,AI X G,et al. Application status and prospect of narrow window control and big data in direct rolling[J]. China Metallurgy,2018,28(9):8.)
[3]	袁晴棠,殷瑞钰,曹湘洪,等. 面向2035的流程制造业智能化目标、特征和路径战略研究[J]. 中国工程科学,2020,22(3):148.(YUAN Q T,YIN R Y,CAO X H,et al. Strategic research on the goals characteristics and paths of intelligentization of process manufacturing industry for 2035[J]. Strategic Study CAE,2020,22(3):148.)
[4]	YIN R Y. Review on the study of metallurgical process engineering[J]. International Journal of Minerals,Metallurgy and Materials,2021,28(8):1253.
[5]	冯梦龙,林路,赵舸,等. LF精炼自动控制技术发展与展望[J]. 中国冶金,2022,32(11):32.(FENG M L,LIN L,ZHAO G,et al. Development and prospect of LF refining automatic control technology[J]. China Metallurgy,2022,32(11):32.)
[6]	PAHLEVANI F,KITAMURA S Y,ITO K,et al. Development of simulation model for hot metal dephosphorization process[J]. Tetsu-to-Hagane,2014,100(4):491.
[7]	王雨墨,陶林,郭皓宇,等. 转炉铁水预处理脱磷的影响因素[J]. 钢铁,2020,55(9):29.(WANG Y M,TAO L,GUO H Y,et al. Dephosphorization influence factors in converter hot metal pretreatment[J]. Iron and Steel,2020,55(9):29.)
[8]	GU K,DOGAN N,COLEY S. The influence of sulfur on dephosphorization kinetics between bloated metal droplets and slag containing FeO[J]. Metallurgical Materials Transactions B,2017,48(5):2343.
[9]	WANG M L,YANG W Y. Dephosphorization in the early stage of converter steelmaking[J]. Ironmaking and Steelmaking,2020,47(10):1127.
[10]	LIU F,WANG G,ZHAO Y,et al. Hot metal dephosphorisation by low basicity slag in the early stage of converting process[J]. Ironmaking and Steelmaking,2019,46(4):392.
[11]	WU W,ZHAO B,ZHAO B,et al. Hot metal dephosphorization process using calcium ferrite slag without fluorite[J]. Ironmaking and Steelmaking,2022,49(7):661.
[12]	赵斌,吴伟,吴巍,等. 不锈钢喷粉吹氧法铁水脱磷工艺[J]. 中国冶金,2022,32(6):155.(ZHAO B,WU W,WU W,et al. Dephosphorization process of hot metal by powder spraying and oxygen blow for stainless steel production[J]. China Metallurgy,2022,32(6):155.)
[13]	赵斌,吴巍,吴伟,等. 铁水脱磷顶吹氧+喷粉搅拌冶炼工艺的应用[J]. 钢铁,2019,54(11):33.(ZHAO B,WU W,WU W,et al. Application of top blowing oxygen and powder injection stirring process for hot metal dephosphorization[J]. Iron and Steel,2019,54(11):33.)
[14]	丁宁,孟义春,李宁,等. 顶吹转炉中高磷铁水脱磷工艺研究[J]. 炼钢,2021,37(5):6.(DING N,MENG Y C,LI N,et al. Study on dephosphorization process with middle and high phosphorus hot metal in top-blowing converter[J]. Steelmaking,2021,37(5):6.)
[15]	智建国,吴伟,高琦,等. 大型转炉优化造渣工艺提高脱磷的效果[J]. 钢铁,2020,55(7):72.(ZHI J G,WU W,GAO Q,et al. Effect of improving dephosphorization of molten steel by optimizing slagging in large converter[J]. Iron and Steel,2020,55(7):72.)
[16]	赵长亮,孙彦辉,袁天祥,等. 转炉预脱磷与“全三脱”铁水少渣冶炼技术[J]. 钢铁,2016,51(5):28.(ZHAO C L,SUN Y H,YUAN T X,et al. Dephosphorization pretreatment in LD converter and less-slag steelmaking process[J]. Iron and Steel,2016,51(5):28.)
[17]	ZHAO B,WU W,WU W,et al. Study on the occurrence of phosphorus in the slag of hot metal dephosphorization for stainless steel production[J]. Steel Research International,2020,91(7):1.
[18]	YE G F,YANG J,ZHANG R H,et al. Behavior of phosphorus enrichment in dephosphorization slag at low temperature and low basicity[J]. International Journal of Minerals Metallurgy and Materials,2021,28(1):66.
[19]	WU W,DAI S F,LIU Y. Dephosphorization stability of hot metal by double slag operation in basic oxygen furnace[J]. Journal of Iron and Steel Research International,2017,24(9):908.
[20]	DAI Y X,LI J,SHI C B,et al. Dephosphorization of high silicon hot metal based on double slag converter steelmaking technology[J]. Ironmaking and Steelmaking,2019,48(4):447.
[21]	ZHANG R H,YANG J,SUN H,et al. Kinetic model of dephosphorization in the new double slag converter steelmaking process[J]. Ironmaking and Steelmaking,2021,48(10):1277.
[22]	王星,胡显堂,危尚好,等. 转炉冶炼低磷洁净钢的工艺开发和实践[J]. 钢铁,2022,57(11):53.(WANG X,HU X T,WEI S H,et al. Process development and practice of converter smelting low phosphorus clean steel[J]. Iron and Steel,2022,57(11):53.)
[23]	周朝刚,陈庆功,艾立群,等. 转炉熔渣低温气化脱磷行为[J]. 钢铁,2022,57(11):64.(ZHOU C G,CHEN Q G,AI L Q,et al. Dephosphorization behavior by low temperature gasification of converter slag[J]. Iron and Steel,2022,57(11):64.)
[24]	HAN X,LI J,ZHOU C G,et al. Study on mineralogical structure of dephosphorisation slag at the first deslagging in BOF steelmaking process[J]. Ironmaking and Steelmaking,2016,44(4):1.
[25]	HAN X,ZHOU C G,LI J,et al. Effect of phase structure of converter dephosphorization slag on dephosphorization[J]. Journal of Iron and Steel Research,2016,28(9):40.
[26]	KITAMURA S Y,SHIBATA H,SHIMAUCHI K I,et al. The importance of dicalcium-silicate on hot metal dephosphorizationreaction[J]. Metallurgical Research and Technology,2008,105(5):263.
[27]	LI J,WANG S J,XIA Y J,et al. Study on dephosphorisation of hot metal pretreatment with Al2O3 to replace CaF2 in slag[J]. Ironmaking and Steelmaking,2015,42(1):70.
[28]	WU W,YANG Q Y,GAO Q,et al. Effects of calcium ferrite slag on dephosphorization of hot metal during pretreatment in the BOF converter[J]. Journal of Materials Research and Technology,2020,9(3):2754.
[29]	HE S,LIN L,LIU Y Q,et al. Experimental study on the preparation of ferrophosphorus alloy using dephosphorization furnace slag by carbothermic reduction[J]. High Temperature Materials and Processes,2022,41:578.
[30]	朱山,张琳,李松. 基于FactSage计算优化转炉脱磷工艺的基础研究[J]. 四川大学学报(自然科学版),2022,59(5):129.(ZHU S,ZHANG L,LI S. Optimization of converter dephosphorization process by simulation calculation based on FactSage[J]. Journal of Sichuan University(Natural Science Edition),2022,59(5):129.)
[31]	SUITO H,INOUE R. Phosphorus distribution between MgO-saturated CaO-FeOt-SiO2-P2O5-MnO slags and liquid iron[J]. Tetsu-to-Hagane,1984,70(2):186.