Opening control of slide gate in continuous casting and analysis of steel spraying |
ZHANG Yumeng1, CHENG Shusen1, FENG Yongping2, LI Jipeng2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2. Carbon Steel and Thin Plate Plant, Jiuquan lron and Steel (Group) Co., Ltd., Jiayuguan 735100, Gansu, China |
|
|
Abstract Factors affecting the opening of slide gate was studied based on Bernoulli's principle, and a feedforward-feedback control scheme of the slide gate was proposed to reduce the hysteresis problem of ladle slide gate feedback control. Meanwhile, the reasons and influencing factors of steel spraying at the joint position of ladle shroud and collective nozzle in the initial teeming stage after the ladle change were analyzed. The results show that the liquid level of ladle decreases gradually under constant casting speed. The opening of slide gate should be increased to stabilize the height of liquid level in the tundish. Reducing the diameter of slide gate and ladle shroud and increasing the argon blowing rate will increase the pressure loss when the molten steel flows through the slide gate, but the immersion depth of the ladle shroud does not affect the pressure loss of molten steel. At the beginning of casting, the gas in the ladle shroud is compressed and heated by the molten steel, so its pressure increases, resulting in steel spraying. Using a trumpet ladle shroud and reducing the immersion depth can make the pressure in the nozzle smaller and reduce the occurrence of steel spraying. This study plays an important role in realizing online real-time stable control of slide gate opening to improve the stability of liquid level in the tundish and finally improve the quality of molten steel.
|
Received: 20 June 2023
|
|
|
|
[1] |
包燕平,王敏. 中间包冶金技术发展趋势[J]. 连铸,2021(5):2.
|
[2] |
唐德池,刘国梁,马文俊,等.控流装置对中间包钢水流场和洁净度的影响[J]. 连铸,2021(5):103.
|
[3] |
刘逸波,杨健. 中间包流场控制技术的进展[J]. 连铸,2021(5):12.
|
[4] |
李林,叶成立,廖凯,等. 自由流动情况下钢包浇注速度的研究[J]. 大型铸锻件,2019(6):9.
|
[5] |
孙继华. 钢包滑动水口机构的应用现状[J]. 冶金设备,2014(2):56.
|
[6] |
刘春青,周立新,王会明,等. 55 t钢包水口用滑动机构的改进[J]. 冶金设备,2005(4):66.
|
[7] |
编辑部. 日本住友金属公司采用滑动水口控制连铸钢水量[J]. 武钢技术,1974(2):68.
|
[8] |
钟巍,徐蕊,王海军,等. 换包过程中连铸中间包内多相流动行为研究[J]. 炼钢,2022,38(4):63.
|
[9] |
张江山,刘青,杨树峰,等. 长水口对连铸中间包钢液保护浇注作用的研究进展[J]. 工程科学学报,2020,42(8):939.
|
[10] |
马续香. 钢包用喇叭形长水口[J]. 钢铁研究学报,1992(2):22.
|
[11] |
赵建辉. 连铸中间包长水口吹氩优化模拟研究[D]. 北京:北京科技大学,2019.
|
[12] |
孙继华. 钢包滑动水口机构的应用现状[J]. 冶金设备,2014(2):56.
|
[13] |
石凯,夏熠. 炼钢用滑动水口材质体系的演变[J]. 耐火材料,2018,52(3):230.
|
[14] |
唐建洪,周玉军,魏海成. 中间包结构及包衬耐火材料对钢水清洁度的影响分析[J]. 世界有色金属,2019(8):194.
|
[15] |
刘鑫,王帅,赵建平,等. 提高中薄板坯连铸机中间包寿命实践[J]. 铸造技术,2021,42(2):128.
|
[16] |
赵青,顾学群. 非晶制带钢水液位的模糊控制[J]. 电气传动,2006(4):36.
|
[17] |
DUSSUD M,GALICHET S,FOULLOY L P. Application of fuzzy logic control for continuous casting mold level control[J]. IEEE Transactions on Control Systems Technology,1998,6(2):246.
|
[18] |
FENG Y,WU M,CHEN X,et al. A fuzzy PID controller with nonlinear compensation term for mold level of continuous casting process[J]. Information Sciences,2020,539:487.
|
[19] |
LEE D,KUEON Y,LEE S. High performance hybrid mold level controller for thin slab caster[J]. Control Engineering Practice,2004,12(3):275.
|
[20] |
WATANABE T,OMURA K,KONISHI M,et al. Mold level control in continuous caster by neural network model[J]. ISIJ International,1999,39(10):1053.
|
[21] |
陈世刚,朱雄辉. 圆方坯连铸机中间包与结晶器的钢水液位控制[J]. 冶金自动化,2011,35(6):47.
|
[22] |
张丽娟,徐勇. 大方坯连铸中间罐滑动水口开度控制装置的调整与应用[J]. 鞍钢技术,2001(2):10.
|
[23] |
SU Z,HE Q,XIE Z. Indirect measurement of molten steel level in tundish based on laser triangulation[J]. Review of Scientific Instruments,2016,87(3):035117.
|
[24] |
黄科元,周滔滔,黄守道,等. 含前馈补偿和微分反馈的数控位置伺服系统[J]. 中国机械工程,2014,25(15):2017.
|
[25] |
OLIA H,YANG H,CHO S M,et al. Pressure distribution and flow rate behavior in continuous-casting slide-gate systems:PFSG[J]. Metallurgical and Materials Transactions B,2022,53(3):1661.
|
[26] |
YANG H,OLIA H,THOMAS B G. Modeling air aspiration in steel continuous casting slide-gate nozzles[J]. Metals,2021,11(1):116.
|
[27] |
黄卫星,伍勇. 工程流体力学[M]. 北京:化学工业出版社,2018.
|
[28] |
BÖHLE M,ETLING D,MÜLLER U,et al. Prandtl's Essentials of Fluid Mechanics[M]. New York:Springer New York,2004.
|
[29] |
EGERTON P,HOWARTH J A,POOTS G,et al. A theoretical investigation of heat transfer in a ladle of molten steel during pouring[J]. International Journal of Heat and Mass Transfer,1979,22(11):1525.
|
[30] |
李卓. 微细通道内单相和两相阻力损失特性的研究[D]. 北京:北京工业大学,2007.
|
[31] |
潘秀兰,王艳红,梁慧智,等. 连铸机浸入式水口堵塞问题分析及其改善措施[J]. 世界钢铁,2010,10(3):22.
|
|
|
|