轧后冷却工艺对大输量X80M管线钢显微组织的影响

doi:10.13228/j.boyuan.issn1006-9356.20230363

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to ensure the high strength of large-transmission X80M pipeline steel and further improve its low temperature toughness, and achieve a good match of strength and toughness, Gleeble-3800 thermal simulation tester was used to simulate rolling. The dynamic CCT curve was established by thermal expansion method combined with microstructure analysis, and the effects of cooling rate and final cooling temperature on the microstructure and hardness were studied by OM, SEM, hardness testing and other analytical methods. The results show that with the increase of cooling rate, the microstructure produces the transition of PF+P→GB→AF→BF, and the Vickers microhardness gradually increases. The ideal microstructure consisting of fine uniform AF and diffusely distributed M/A islands can be obtained when the cooling rate is in the range of 15-25 ℃/s. Final cooling temperature has an obvious effect on its phase composition. As the final cooling temperature decreases, the M/A island size becomes smaller, the number increases and its microstructure gradually refines. Combining experimental research with production practice, the final industrialized TMCP parameters are set to final rolling temperature of 780 ℃+final cooling temperature of 360 ℃+cooling speed of 20 ℃/s. The obtained X80M pipeline steel coil has high strength and excellent low temperature toughness, which meets its engineering and technical requirements, and is successfully applied in the major pipeline project of West-East Gas Transmission Line IV. This study provides technical reference for the research and development of high-strength and high-toughness pipeline steel and strongly supports the construction of national major pipeline projects.

Key words： large-transmission X80M pipeline steel CCT curve cooling rate post-rolling cooling process acicular ferrite

Received: 06 June 2023

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Gan
	KONG Xianglei
	HUANG Minghao
	WANG Yang
	ZHANG Yinghui

Cite this article:

LIU Gan,KONG Xianglei,HUANG Minghao等. Effect of post-rolling cooling process on microstructure of large-transmission X80M pipeline steel[J]. China Metallurgy, 2023, 33(11): 81-87.

URL:

http://www.zgyj.ac.cn/EN/10.13228/j.boyuan.issn1006-9356.20230363 OR http://www.zgyj.ac.cn/EN/Y2023/V33/I11/81

[1]	王晓香. 国内外超大输量天然气管道建设综述[J]. 焊管,2019,41(7):1.
[2]	刘宇,张立忠,高维新. 管线钢的历史沿革及未来展望[J]. 油气储运,2022,41(12):1355.
[3]	徐景涛. X80管线钢在长输管道中的应用及展望[J]. 中国冶金,2016,26(8):1.
[4]	郑磊,傅俊岩. 高等级管线钢的发展现状[J]. 钢铁,2006,41(10):10.
[5]	WANG W,SHAN Y Y,YANG K. Study of high strength pipeline steels with different microstructures[J]. Materials Science and Engineering A,2009,502(1/2):38.
[6]	周文浩. 大壁厚大口径X80M管线钢DWTT性能的控轧工艺试验研究[J]. 材料科学与工艺,2022,30(6):82.
[7]	王明明,高秀华,杜林秀,等. V-N微合金化X80抗大变形管线钢的组织与力学性能[J]. 东北大学学报(自然科学版),2020,41(6):801.
[8]	尹雨群,雷玄威,吴开明. 超高强度管线钢的开发现状与趋势[J]. 中国冶金,2012,22(9):5.
[9]	王志勇,李少坡,李群,等. 经济型X80管线钢的研制开发[J]. 中国冶金,2016,26(11):64.
[10]	蔡绪明,李艳梅,李中平,等. 不同冷却方式下X80M管线钢的组织演变[J]. 轧钢,2023,40(1):41.
[11]	ZHENG X F,KANG Y L,MENG D L,et al. Effect of cooling start temperature on microstructure and mechanical properties of X80 high deformability pipeline steel[J]. Journal of Iron and Steel Research International,2011,18(10):42.
[12]	WU Q,HE S,HU P,et al. Effect of finish rolling temperature on microstructure and mechanical properties of X80 pipeline steel by on-line quenching[J]. Materials Science and Engineering A,2023,862:144496.
[13]	褚峰,张继明,张亚运,等. 中俄东线大壁厚X80管线钢的连续冷却相变行为[J]. 热加工工艺,2020,49(20):146.
[14]	ZENG Y,ZHU P,TONG K. Effect of microstructure on the low temperature toughness of high strength pipeline steels[J]. International Journal of Minerals Metallurgy and Materials,2015,22(3):254.
[15]	段贺,单以银,杨柯,等. X80低温用高强度管线钢的工艺与组织性能试验[J]. 钢铁,2020,55(2):107.
[16]	牛延龙,刘清友, 贾书君,等. X80级高强低合金管线钢组织与冲击韧性[J]. 钢铁,2019,54(2):9.
[17]	WANG B,LIAN J. Effect of microstructure on low-temperature toughness of a low carbon Nb-V-Ti microalloyed pipeline steel[J]. Materials Science and Engineering A,2014,592:50.
[18]	刘妍,王栋,王建钢,等. 轧后冷却速率对22 mm厚X80M热轧带钢组织和力学性能的影响[J]. 机械工程材料,2020,44(2):49.
[19]	HUDA N,MIDAWI A R H,GIANETTO J,et al. Influence of martensite-austenite (MA) on impact toughness of X80 line pipe steels[J]. Materials Science and Engineering A,2016,662:481.
[20]	DUAN H,SHAN Y,YANG K,et al. Effect of rare earth and cooling process on microstructure and mechanical properties of an ultra-cleaned X80 pipeline steel[J]. Acta Metallurgica Sinica (English Letters),2021,34(5):639.
[21]	谌铁强,宋欣,张国栋,等. 不同控冷模式对X80管线钢组织性能的影响[J]. 轧钢,2015,32(4):24.
[22]	牛延龙,刘清友,贾书君,等. 控冷工艺下组织及M/A岛对管线钢韧性的影响[J]. 钢铁,2020,55(6):10.
[23]	刘振华,曲之国,王川,等. 30.2 mm厚规格X80M钢板的研制与开发[J]. 轧钢,2023,40(2):125.
[24]	洪良,左秀荣,姬颍伦,等. 厚规格X80管线钢低温断裂行为研究[J]. 材料研究学报,2018,32(1):9.
[25]	李龙飞,张阳,林腾昌,等. 含钒X80级管线钢奥氏体晶粒长大行为[J]. 钢铁,2022,57(1):9.
[26]	ROCCISANO A,NAFISI S,STALHEIMD,et al. Effect of TMCP rolling schedules on the microstructure and performance of X70 steel[J]. Materials Characterization,2021,178:111207.
[27]	ZHOU F,LI L J,GAO J X,et al. Effect of ultra fast cooling coiling temperature on microstructures and properties of X80 pipeline steel[C]//5th Annual International Conference on Material Science and Engineering (ICMSE2017). Xiamen:[s.n.],2017:012037.