Application of surface inspection system in detection of linear defects on cold-rolled sheets |
WANG Lin1, YU Yang1, NI You-jin2, FU Guang2, WANG Chang1, GAO Xiao-li1 |
1. Department of Thin Sheet, Research Institute of Technology of Shougang Group Co., Ltd., Beijing 100043, China; 2. Manufacturing Department, Beijing Shougang Co., Ltd., Qian′an 064404, Hebei, China |
|
|
Abstract Mold flux defect, bubble defect, inclusion defect and cold rolling scratches are the four typical linear defects on the surface of cold-rolled sheets. Due to the similarity of the macroscopic morphology for these four defects, it is difficult to accurately distinguish them by surface inspection system, which causes difficulty in the judgment, traceability and process improvement. The surface inspection results, physical morphologies and microscopic characteristics of each linear defect were compared through large numbers of sampling analysis, and the macroscopic and microscopic characteristics of every kind of linear defect were clarified. Based on this, the judgment rules and the defect library of the surface inspection system are optimized, thus the accuracy rate of defect judgment is improved from 80% to 90%.
|
Received: 27 May 2022
|
|
|
|
[1] |
苗峰.热镀锌表面缺陷分析及控制[J].工业技术,2012(8):95.
|
[2] |
曾松盛,成小军,周明伟,等.Q345B热轧板板面结疤缺陷产生原因分析[J].中国冶金,2012,22(2):14.
|
[3] |
刘红冰.基于神经网络的冷轧带钢表面缺陷检测与分类技术研究[D].成都:电子科技大学,2005.
|
[4] |
邓小旋,季晨曦,王胜东,等.冷轧薄板线状缺陷的工艺控制[J].中国冶金,2017,27(4):55.
|
[5] |
王畅,于洋,王林,等.热轧卷表面机清条纹的形成机理与预防措施[J].中国冶金,2018,28(7):46.
|
[6] |
刘小军,李斌,顾晓琳,等.Cognex表面检测仪在八钢 1 750 mm 热轧的应用[J].新疆钢铁,2010(3):11.
|
[7] |
张丹,叶校瑛,任秋红,等.双传感器表面检测系统在镀锌线上的应用[J].中国冶金,2017,27(9):48.
|
[8] |
刘延强,杨敬铭,单伟,等.热轧卷表面线状缺陷分析[J].中国冶金,2016,26(7):48.
|
[9] |
罗衍昭,田志红,李向奎,等.超低碳IF钢中夹杂物来源的示踪分析[J].中国冶金,2019,29(9):56.
|
[10] |
高荣正,刘中秋,李宝宽,等.超低碳钢连铸坯表层气泡缺陷的分布特征[J].炼钢,2021,37(6):45.
|
[11] |
王田田,杨树峰,李京社,等.连铸坯皮下气泡缺陷成因及控制[J].中国冶金,2020,30(12):35.
|
[12] |
邱涛.H08A焊条钢工艺及质量控制[J].中国冶金,2018,28(11):45.
|
[13] |
肖寄光,王福明.连铸坯中气泡产生原因分析及判断方法[J].宽厚板,2006,12(2):32.
|
[14] |
安超,黄财德,单伟,等.首钢京唐IF钢生产工艺开发实践[J].炼钢,2019,35(6):52.
|
|
|
|