Effect of surface treatment on pitting corrosion resistance of 316L stainless steel for offshore engineering |
ZHONG Qiang1,2, QIAN Jiong1,2, WU Jing-na1, ZHAO Xin-hua1, MA Rong-li1, LIU Zheng-dong1 |
1. Zhejiang Jiuli Hi-Tech Metals Co., Ltd., Huzhou 313028, Zhejiang, China; 2. Jiuli International Science and Technology Cooperation Base for Special Alloy Material Corrosion and Protection, Huzhou 313028, Zhejiang, China |
|
|
Abstract 316L stainless steel is a commonly used corrosion-resistant alloy material, however, it is prone to pitting corrosion in the marine and atmospheric service environment. The pitting corrosion resistance of 316L tubes after various surface treatments (bright annealing, polishing and pickling passivation) was evaluated by pitting rate, critical pitting temperature, pitting potential and polarization curve test. The results show that different surface treatments have no significant influence on the critical pitting temperature, but the pitting rate and pitting potential will differ. Polishing and pickling passivation can effectively improve the pitting corrosion resistance of 316L stainless steels, of which the pickling passivation state has the best pitting resistance, so it is recommended that the 316L stainless steel products for offshore engineering should be pickling passivation treatment before use.
|
Received: 21 February 2022
|
|
|
|
[1] |
李灏,柴锋,何宜柱,等. 环境温度对船用耐蚀钢腐蚀行为的影响[J]. 钢铁,2013,48 (8):65.
|
[2] |
郭慧英,张宇,何玉春,等. 低合金耐海水腐蚀钢的开发[J]. 钢铁,2013,48 (9):71.
|
[3] |
胡津津,石明伟. 海洋平台的腐蚀与防腐技术[J]. 中国海洋平台,2008,23(6):39.
|
[4] |
周敏. 海水淡化工程中管道材料选用[J]. 腐蚀与防护,2006,27(10):536.
|
[5] |
陈艳艳,华斌,孔振英,等. 海上平台消防水系统管材选择[J]. 中国造船,2008,49(增刊):509.
|
[6] |
孔韦海,艾志斌,万章,等. 电位对S22053不锈钢在6%FeCl3溶液中耐腐蚀性能的影响[J]. 材料保护,2019,52(7):48.
|
[7] |
程从前,付琴琴,曹铁山,等. 钝化膜质量对奥氏体不锈钢耐蚀性的影响及显色检测[J]. 材料工程,2013(8):69.
|
[8] |
王威. 316L不锈钢点蚀的电化学行为及其影响因素研究[D]. 成都:西南石油大学,2014.
|
[9] |
张云乾,马向阳,陶鑫. 电化学钝化技术在田湾核电站不锈钢管道的应用[J]. 全面腐蚀控制,2019,33(2):12.
|
[10] |
林泽泉,刘爽,孙志强,等. 核电厂反冲洗海水管道内壁防腐蚀处理技术的应用[J]. 腐蚀与防护,2014,35(12):1263.
|
[11] |
张瑜,孔令真,路伟,等. 在硝酸溶液中不锈钢表面钝化膜的电化学特性[J]. 腐蚀与防护,2018,39(12):906.
|
[12] |
信息产业部工艺标准化技术委员会. SJ 20893—2003 不锈钢酸洗与钝化规范[S].
|
[13] |
美国材料与试验协会. ASTM G48—2011 Resistance of Stainless Steel and Related Alloys by Use of Ferric Chloride Solution[S].
|
[14] |
国家质量技术监督局. GB T 17899—1999 不锈钢点蚀电位测量方法[S].
|
[15] |
桂艳,高岩. 不锈钢表面钝化膜特性的研究进展[J]. 特殊钢,2011,32(3):20.
|
[16] |
王梅丰,李光东,杜楠. 表面粗糙度对304不锈钢早期点蚀行为影响的电化学方法[J]. 失效分析与预防,2012,7(2):86.
|
[17] |
曹楚南. 腐蚀电化学原理[M]. 北京:化学工业出版社,2004.
|
[18] |
李云超,严川伟,张伟. 不锈钢电极在交变电场作用下的反应机制[C]//全国腐蚀电化学及测试方法专业委员会2002年学术交流会议论文集. 沈阳:全国腐蚀电化学及测试专业委员会,2002:9.
|
[19] |
Olsson C,Landolt D.Passive films on stainless steels—chemistry,structure and growth[J].Electrochimica Acta,2003,48(9):1093.
|
[20] |
Vayer M,Reynaud I,Erre R.XPS characterisations of passive films formed on martensitic stainless steel:qualitative and quantitative investigations[J].Journal of Materials Science,2000,35(10):2581.
|
|
|
|