Microstructure and properties of new stainless steel for corrosion resistant heating pipe |
ZHAO Lei1, YAN Hai-tao1,2, MA Deng-de1, SHEN Peng1, LI Jie1, LIANG Cui-feng1 |
1. Zhenshi Group Eastern Special Steel Co., Ltd., Jiaxing 314005, Zhejiang, China; 2. Zhenshi Group HuaZhi Research Institute (ZheJiang) Co., Ltd., Jiaxing 314505, Zhejiang, China |
|
|
Abstract Stainless steel materials for electric water heater mainly include 310S、840 and other materials. During the process of using, the electric heating pipe is easy to scale, resulting in corrosion failure of heating pipe. In order to solve this problem, according to the service environment of heating pipe, Mo element was added on the basis of 310S composition system, other alloy composition systems were also optimized and adjusted, and a new stainless steel material for corrosion-resistant heating pipe was developed. The microstructure, mechanical properties and corrosion properties of a new type heating tube stainless steel in hot rolling solution pickling state were studied and compared with 310S steel. The change law of alloy structure with temperature under equilibrium condition was analyzed by Thermo-Calc thermodynamic software. It is shown that the σ phase precipitation begin at about 900 ℃, but the number is small. Under the same rolling procedure and heat treatment procedure as 310S, the average values of tensile strength (Rm), yield strength (Rp0.2) and elongation of hot-rolled solid solution pickling state of the new material are 611 MPa, 286 MPa, 52.8%, respectively. The overall strength is slightly higher than 310S, but the difference is small, and the elongation is slightly lower than 310S. The grain size of the new material is grade 5.5 and grade 7 in some areas. The grain size is slightly bigger than 310S, and there is little difference in whole. The average corrosion rates of new materials and 310S are 0.49 g/(m2·h) and 1.37 g/(m2·h) respectively. It can be seen that the pitting corrosion resistance of new materials is significantly better than 310S steel.
|
Received: 17 February 2022
|
|
|
|
[1] |
潘钱付,刘超红,唐睿,等.Ti、Zr微合金化310S不锈钢的制备研究[J].核动力工程,2012,33(增刊2):70.
|
[2] |
高福彬,杨吉春.新型310S耐热钢组织和高温力学性能[J].金属热处理,2014,39(11):30.
|
[3] |
梁成浩,张国庆.用电化学技术评价310不锈钢的高温损伤[J].金属热处理学报,2000,21(1):20.
|
[4] |
马艳丽,徐斌,李具仓.310S耐热奥氏体不锈钢连铸坯研究[J].铸造,2015,64(5):463.
|
[5] |
秦丽雁.不锈钢应用中的几个腐蚀问题研究[D].天津:天津大学,2006.
|
[6] |
喇培清,张鹏,刘辉,等.固溶处理对高铝310S钢组织和性能的影响[J].材料热处理学报,2014,35(3):73.
|
[7] |
李鹏燕,熊毅,陈路飞,等.深冷轧制对AISI 310S不锈钢组织和性能的影响[J].材料热处理学报,2015,36(3):112.
|
[8] |
喇培清,刘辉,孟倩,等.不同Al含量的310S耐热钢热轧加工后的组织和力学性能[J].兰州理工大学学报,2012,38(5):15.
|
[9] |
张庆.热处理对AISI 310S不锈钢在不同介质中的腐蚀磨损行为的影响[D].镇江:江苏大学,2016.
|
[10] |
熊毅,陈路飞,王俊北,等.退火对深冷轧制AISI310S奥氏体不锈钢组织和耐蚀性能的影响[J].材料热处理学报,2016,37(2):65.
|
[11] |
Tavares S S M,Moura V,Da Costa V C,et al.Microstructural changes andcorrosion resistance of AISI 310S steel exposed to 600-800 ℃[J].MaterialsCharacterization,2009,60(6):573.
|
[12] |
武晋花.用电化学方法测量不锈钢晶间腐蚀的敏感性[J].冶金标准化与质量,2001(3):12.
|
[13] |
查小琴,邵军,张利娟.不锈钢晶间腐蚀测试方法[J].材料开发与应用,2009,24(3):60.
|
[14] |
LI H B, JIANG Z H, ZHANG Z R, et al.Intergranular corrosion behavior of high nitrogen austenitic stainless steel[J].International Journal of Minerals,Metallurgy and Materials,2009,16(6):654.
|
[15] |
曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2001.
|
[16] |
刘同华,强文江,王伟.不锈钢中合金元素的作用及其研究现状[J].热加工工艺,2018,47(4):5
|
[17] |
庞宗旭,王勇,胡昕明,等. S31609奥氏体不锈钢中残留δ铁素体的腐蚀行为[J].中国冶金,2021,31(3):59.
|
|
|
|