电梯用含氮节镍奥氏体不锈钢QN1701的组织和性能

doi:10.13228/j.boyuan.issn1006-9356.20220184

Abstract
Figure/Table
References
Related Citation (2)

Download: PDF (6874 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract Nitrogen contained low nickel austenitic stainless steel QN1701(12Cr17Mn7Ni2Cu2N)was designed by Thermo-Calc software to replace 443(019Cr21CuTi) ultra pure ferritic stainless steel for elevator. Microstructure and properties of QN1701 and 443 stainless steel were investigated by means of OM, SEM, Electrochemical workstation and other methods. It was shown that yield strength of QN1701 stainless steel was increased to more than 400 MPa and was 1.32 times of that of 443 stainless steel for nitrogen playing a role of grains refining and solution strengthening. The pitting potential of QN1701 stainless steel was 241 mV, which was lower than 289 mV of 443 stainless steel, but its pitting rate was 9.10 g/(m²·h), which was lower than 14.58 g/(m²·h) of 443 stainless steel. The corrosion resistance of QN1701 stainless steel was significantly better than that of 443 stainless steel in the accelerated corrosion tests with environment of 10%NaCl neutral salt spray and cyclic exposure of wet and dry salt spray under the condition of grinding and wire drawing surface for elevator plate. The analysis found that (Nb,Ti) (C,N) precipitations generated by adding a certain amount of Nb and Ti to 443 stainless steel after grinding and wire drawing process, exposed to the surface or left a small pit after being dragged, which led its corrosion resistance to be reduced. In conclusion, QN1701 stainless steel has the characteristics of higher strength, elongation and better corrosion resistance on wire drawing surface, which is of great value for the light-weight design and longer service life of elevator.

Key words： nitrogen contatined low nickel austenitic stainless steel solubility wire drawing surface salt spray test lightweight design

Received: 24 February 2022

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	JIANG Yi
	SHI Xian-yun
	JIANG Lai-zhu
	KONG Qing-mao
	JIANG Mei-xue
	ZHENG Lan-zhen

Cite this article:

JIANG Yi,SHI Xian-yun,JIANG Lai-zhu等. Microstructure and properties of nitrogen contained low nickel austenitic stainless steel QN1701 for elevator[J]. China Metallurgy, 2022, 32(6): 108-116.

URL:

http://www.zgyj.ac.cn/EN/10.13228/j.boyuan.issn1006-9356.20220184 OR http://www.zgyj.ac.cn/EN/Y2022/V32/I6/108

[1]	王宇,彭翔飞,李俊,等.高氮奥氏体不锈钢强韧化及抗弹性能研究进展[J].钢铁,2022,57(1):28.
[2]	王祥元.节镍型高氮奥氏体不锈钢热变形行为的研究[J].冶金与材料,2019,39(4):41.
[3]	Shin J H, Lee J, Min D J, et al. Solubility of nitrogen in high manganese steel (HMNS) melts:Interaction parameter between Mn and N[J].Metallurgical and Materials Transactions,2011,B42(6):1081.
[4]	王梅丰,李光东,杜楠.表面粗糙度对304不锈钢早期点蚀行为影响的电化学方法[J].失效分析与预防,2012,7(2):86.
[5]	Feichtinger H K, Stein G. Melting of high nitrogen steels[J].Materials Science Forum,1999(318):261.
[6]	郎宇平,陈海涛,翁宇庆,等.热力学计算在高氮奥氏体不锈钢研究中的应用[J].材料工程,2013(5):16.
[7]	李长荣,杨小平,文辉.铜元素在钢表面氧化过程中富集规律的研究[J].热加工工艺,2010,39(4):8.
[8]	薛忍让,宋志刚,郑文杰,等.氮对316L晶粒尺寸和力学性能的影响[J].钢铁研究学报,2013,25(10):36.
[9]	邓亚辉,杨银辉,曹建春,等.23Cr-2.2Ni-6.3Mn-0.26N节Ni型双相不锈钢动态再结晶行为研究[J].金属学报,2019,55(4):445.
[10]	蒋一,程满浪,姜海洪,等.高强度含N节Ni奥氏体不锈钢08Cr19Mn6Ni3Cu2N(QN1803)的显微组织及性能[J].金属学报,2020,56(4):642.
[11]	Singh B B, Sukumar G, Paman A, et al.A comparative study on the ballistic performance and failure mechanisms of High-Nitrogen Steel and RHA Steel against tungsten heavy alloy penetrators[J].Journal of Dynamic Behavior of Materials,2021,7(1):60.
[12]	翁建寅,董瀚,李北,等.N含量对高氮CrMnMo奥氏体不锈钢组织和性能的影响[J].金属热处理,2020,45(1):160.
[13]	张钧林.材料科学基础[M].北京:化学工业出版社,2006.
[14]	张荣华,杨川,石宁,等.高氮奥氏体钢的塑性加工变形特性研究进展[J].材料导报,2021,35(11):11155.
[15]	陆世英.不锈钢概论[M].北京:化学工业出版社,2013.
[16]	张宝宏,丛文博,杨萍.金属电化学腐蚀与防护[M].北京:化学工业出版社,2005.
[17]	邹勇.TTS443高铬铁素体不锈钢的开发[J].特殊钢,2012,33(1):51.
[18]	任娟红,陈安忠,李照国,等.439超纯铁素体不锈钢耐蚀性评价[J].中国冶金,2018,28(3):35.
[19]	陈昊,周学杰,吴军,等.2种表面处理304不锈钢在文昌和武汉大气环境中的腐蚀行为研究[J].材料保护,2021,54(5):35.
[20]	南海.TiN夹杂物对超纯铁素体不锈钢点蚀的影响[J].腐蚀与防护,2021,42(9):22.