| Influence of coiling temperature on properties of hot-rolled high strength steel used for mixing tank |
| WANG Yue-yao1,2, HE Qing1,2, ZHAO Zheng-zhi1,2, ZHANG Ming-bo3, BAO Kuo3, HUANG Yao4 |
1. Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China;
2. Beijing Laboratory of Metallic Materials and Processing for Modern Transportation, Beijing 100083, China;
3. Chengde Branch, Hebei Iron and Steel Co., Ltd., Chengde 067102, Hebei, China;
4. China Electric Power Research Institute, Beijing 100192, China |
|
|
|
|
Abstract The effects of different coiling temperatures on the microstructure and properties of C-Si-Mn-Al hot-rolled high strength steel used for mixing tank were studied in the laboratory. And the structure and mechanical properties of the tested steels at different coiling temperatures were analyzed and studied by several techniques such as laser scanning confocal microscope (LSCM), scanning electron microscope (SEM), and electron backscatter diffraction (EBSD). The experimental results showed that ferrite and pearlite were obtained by coiling at 580 and 550 ℃. Ferrite and bainite were obtained at 400 ℃. Ferrite, bainite and martensite were obtained at 300 ℃. And Ferrite and martensite were obtained at 150 ℃. As the coiling temperature decreased, the tensile strength and hardness of the tested steel gradually increased, and the elongation gradually decreased. The tensile strength of the tested steel coiled at 300 ℃ was 1 029 MPa and the Vickers hardness was 342.6. The tensile strength coiled at the 150 ℃ was as high as 1 265 MPa, the Vickers hardness reached 360.7, and the yield ratio reached the lowest, only 0.58.
|
|
Received: 02 September 2019
|
|
|
|
| [1] |
杜秀川,吴刚. 减量化汽车机械搅拌罐用钢开发[J]. 鞍钢技术,2018(5):21.
|
| [2] |
杨雄,敬鑫,姜秉坤. 包钢混凝土搅拌罐用热轧钢带开发[J]. 包钢科技,2018,44(2):58.
|
| [3] |
Bhadeshia H K D H,Edmonds D V. Analysis of mechanical properties and microstructure of high-silicon dual-phase steel[J]. Metal Science, 1980, 14(2):41.
|
| [4] |
尹云洋,杨王玥,李龙飞,等. 基于动态相变的热轧C-Mn-Al-Si系TRIP钢组织演变[J]. 金属学报,2008,44(6):686.
|
| [5] |
尹云洋,杨王玥,李龙飞,等. Al部分替代Si对基于动态相变热轧TRIP钢组织控制的影响[J]. 金属学报,2008,44(11):1292.
|
| [6] |
Kobayashi J,Nakashima Y,Sugimoto K I,et al. Formabilities of C-Si-Al-Mn transformation-induced plasticity-aided martensitic sheet steel[J]. Materials Science Forum, 2016(838/839):546.
|
| [7] |
Hsieh C C,Liu Y C,Wang J S,et al. Microstructural evolution with various Ti contents in Fe-based hardfacing alloys using a GTAW technique[J]. Metals and Materials International, 2014,20(4):701.
|
| [8] |
方圆,张宏艳,崔阳,等. 微量钛对C-Si-Mn-B钢组织和性能的影响[J]. 物理测试,2013,31(6):5.
|
| [9] |
徐洋,孙明雪,周砚磊,等. (Nb,Ti)C在轧后卷取中的析出及对铁素体相微观力学特征的影响[J]. 金属学报,2015,51(1):31.
|
| [10] |
王墉哲,刘俊亮. 回火温度对TiC增强耐磨钢TiC粒子析出行为的影响[J]. 钢铁研究学报,2015,27(8):59.
|
| [11] |
Moor E D,Matlock D K,Speer J G,et al. Austenite stabilization through manganese enrichment[J]. Scripta Materialia,2011,64(2):185.
|
| [12] |
康永林,邝霜,尹显东,等. 汽车用双相钢板的开发与研究进展[J]. 汽车工艺与材料,2006(5):1.
|
| [13] |
沈保罗,李莉,岳昌林. 钢铁材料抗拉强度与硬度关系综述[J]. 现代铸铁,2012, 32(1):93.
|
| [14] |
于庆波,段贵生,孙莹,等. 粒状贝氏体组织对低碳钢力学性能的影响[J]. 钢铁,2008,43(7):68.
|
| [15] |
Bhowmik A,Stone H J. A study on the influence of Mo, Al and Si additions on the microstructure of annealed dual phase Cr-Ta alloys[J]. Journal of Materials Science,2013,48(8):3283.
|
| [16] |
卢叶茂,梁益龙,龙绍檑,等. 淬火20CrNi2Mo低碳钢中大角度晶界对强度的影响[J]. 材料导报,2018,32(24):132.
|
| [17] |
李昭东. 变形和合金元素对钢中奥氏体组织形成和分解相变的影响[D].北京:清华大学, 2011.
|
| [18] |
Morito S,Tanaka H,Konishi R,et al. The morphology and crystallography of lath martensite in Fe-C alloys[J]. Acta Materialia,2003,51(6):1789.
|
| [19] |
Kitahara H,Ueji R,Tsuji N,et al. Crystallographic features of lath martensite in low-carbon steel[J]. Acta Materialia,2006,54(5):1279.
|
| [20] |
Koyama M,Akiyama E,Sawaguchi T,et al. Hydrogen-induced cracking at grain and twin boundaries in an Fe-Mn-C austenitic steel[J]. Scripta Materialia,2012,66(7):459.
|
|
|
|
2020, Vol. 30 