| MPa Grade Cold-Rolled Dual-Phase Steel Continuous Annealing Process in Hansteel |
| PENG Zhao-feng，LIN Zhang-guo，GU Feng-long，HE Fang，LI Shou-bin |
| Handan Iron and Steel Group Co.， Ltd.， Handan, 056015， Hebei， China |
|
|
|
|
Abstract According to DIL805-A, the CCT curve of C-Si-Mn content 600MPa grade cold-rolled dual-phase steel was measured. The annealing process was simulated on Gleeble3500. The results show: The soaking temperature was 800-820℃, soaking time was≥2min, slow cooling temperature is 650-700℃, fast cooling temperature was ≤330℃, cooling rate was ≥15℃/s. According to the EBSD, the TEM, and the tension test. The properties of the 600MPa grade cold-rolled dual-phase steel are: the volume fraction of martinet is about 18%, the value of {111} texture is 5.3, the martinet is low carbon martinet, yield strength was 344-365MPa, tensile strength was 605-645MPa, elongation was 24.5% to 27%. The mechanical property can meet the requirements of making the safety parts of automotive.
|
|
Received: 07 June 2013
Published: 10 April 2014
|
|
Corresponding Authors:
He Fang
E-mail: funy4587@hotmail.com
|
|
|
|
|
|
|
2014, Vol. 24 