板坯动态二冷配水系统的开发与应用
李峰,张炯明
北京科技大学冶金与生态工程学院,北京 100083
Study and Implement of Dynamic Secondary Cooling System for Slab Caster
LI Feng,ZHANG Jiongming
Metallurgy and Ecology Engineering School, University of Science and Technology Beijing, Beijing 100083, China
摘要 建立了板坯凝固数学模型且采取坯龄模型实现动态配水;通过模拟拉速的变化,说明了用于校正有效拉速的速度权重,以及根据目标温度来校正冷却水对坯龄模型的必要性;编制了动态与静态结合的配水系统软件并应用于现场;评价了动态配水的效果。
关键词 :
板坯连铸 ,
坯龄模型 ,
二冷动态配水
Abstract :A residence time model was developed to implement dynamic secondary cooling. It was found by simulating speed change that a parameter is needed to modify the effective speed and water flow needs to be adjusted based on the target surface temperature. Finally, a dynamic and static secondary cooling control system was founded, applied and evaluated.
Key words :
slab casting
residence time model
dynamic secondary cooling
收稿日期: 1900-01-01
[1]
潘贻芳, 祭程, 张晓博, 蔡兆镇, 罗森, 朱苗勇. 宽厚板坯连铸二冷工艺开发与应用 [J]. Journal of Materials Sciences & Technology, 2012, 22(9): 42-46.
[2]
王洪兴, 刘志国. 板坯连铸机粘结漏钢分析与预防措施 [J]. Journal of Materials Sciences & Technology, 2011, 21(9): 30-35.
[3]
林晓川,李京社. 板坯连铸结晶器内钢液表面流速的水模型研究 [J]. Journal of Materials Sciences & Technology, 2010, 20(12): 15-19.
[4]
王永胜. 高拉速板坯连铸结晶器液面波动影响因素研究 [J]. Journal of Materials Sciences & Technology, 2009, 19(9): 24-24.
[5]
白永强,程树森. 板坯连铸结晶器内非对称流动对渣钢界面的影响 [J]. Journal of Materials Sciences & Technology, 2008, 18(6): 1-1.
[6]
王义芳,郝华强,何金贤. 中薄板坯连铸结晶器浸入式水口的优化设计 [J]. Journal of Materials Sciences & Technology, 2008, 18(4): 25-25.
[7]
魏励,杨海滨. 连铸含铌钢板坯表面横裂纹原因分析和措施 [J]. Journal of Materials Sciences & Technology, 2008, 18(12): 17-17.
[8]
杨俊锋. 板坯连铸机高连拉炉数的生产实践 [J]. Journal of Materials Sciences & Technology, 2007, 17(9): 9-9.
[9]
裴凤娟1 ,陈伟庆1 ,候成2 ,杨荣光2 ,王国连2. CASOB精炼和连铸过程钢中夹杂物来源示踪研究 [J]. Journal of Materials Sciences & Technology, 2007, 17(7): 47-47.
[10]
朱开军,任建义,曾扩军. 板坯连铸漏钢的探讨 [J]. Journal of Materials Sciences & Technology, 2007, 17(7): 58-58.
[11]
杜洪波,杨杰. SPHD薄板坯连铸漏钢原因分析及控制措施 [J]. Journal of Materials Sciences & Technology, 2007, 17(6): 59-59.
[12]
张正祥1 ,焦国华1 ,成小军1 ,温德智1 ,孙彦辉2 ,吴光亮1,3. CSP板卷边部缺陷的研究 [J]. Journal of Materials Sciences & Technology, 2007, 17(4): 26-26.
[13]
高仲,张兴中,姚书芳. 薄板坯表面纵裂研究进展 [J]. Journal of Materials Sciences & Technology, 2007, 17(12): 4-4.
[14]
王小燕1 , 肖丽俊2 , 仇圣桃2 , 吴文林1. 硼微合金化对CSP生产低碳铝镇静钢带力学性能的影响 [J]. Journal of Materials Sciences & Technology, 2006, 16(7): 1-1.
[15]
张 文1, 吝章国2, 张 梅1, 李向奎2, 杨林浩2, 孙洪利2, 王习东1 . 邯钢CSP工艺过程钢中夹杂物热力学分析与研究
[J]. Journal of Materials Sciences & Technology, 2006, 16(6): 1-1.