Analysis of strength and desulfurization performance of reconstituted activated carbon powder proportioned with raw coal
LI Xiao-long1,2, WEI Jin-chao1,2, ZHU Cheng3, XU Bing3, CUI Ze-xing1,2
1. Engineering Technology Research Center, Zhongye Changtian International Engineering Co., Ltd., Changsha 410205, Hunan, China; 2. Key Laboratory of Hunan Province for the Synergetic Control and Resource Reuse of the Multi-pollutants of Flue Gas, Changsha 410205, Hunan, China; 3. Industrial Environmental Protection Department, Baowu Group Environmental Resources Technology Co., Ltd., Shanghai 201900, China
Abstract:Activated carbon for granular desulfurization and denitrification was prepared from raw coal, coal tar, asphalt and activated carbon powder. The effects of different activated carbon powder additions on the reconstituted strength and desulfurization performance were investigated. The research showed that with the increase of the amount of activated carbon powder, the wear resistance and compressive strength of the reconstituted desulfurization and denitration activated carbon showed a downward trend. The desulfurization value increased gradually with the increase of the activated carbon powder amount. The desulfurization and denitration activated carbon with excellent product performance and high resource recovery rate can be prepared under the condition that the carbon powder in the mixed coal powder was 15%-23%. The corresponding wear resistance, compressive strength and desulfurization value range were 97.01%-97.40%, 56.63-63.57 daN and 28.92-29.54 mg/g, respectively.
李小龙, 魏进超, 朱诚, 徐兵, 崔泽星. 活性炭粉配煤再造粒强度及其脱硫性能分析[J]. 中国冶金, 2020, 30(3): 69-73.
LI Xiao-long, WEI Jin-chao, ZHU Cheng, XU Bing, CUI Ze-xing. Analysis of strength and desulfurization performance of reconstituted activated carbon powder proportioned with raw coal[J]. China Metallurgy, 2020, 30(3): 69-73.