Thermal stress analysis during service of side sealing plate for thin strip continuous casting
GUO Hai-rong1, LI Xin2, LI Hua-long1, SHI Yi-xin1, YANG Wen-gang3, LI Hong-xia3
1. Institute of Research of Iron and Steel, Shasteel, Suzhou 215625, Jiangsu, China; 2. School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001, Henan, China; 3. State Key Laboratory of Advanced Refractories, Sinosteel Luoyang Institute of Refractories Research Co., Ltd., Luoyang 471039, Henan, China
Abstract:In order to solve the problem of cracking caused by excessive thermal stress during the service process of the side sealing plate for thin strip continuous casting, the numerical simulation method was adopted, and the thermal-structural coupling analysis was carried out to study the effect of different material parameters and preheating temperature of the BN-based side sealing plate on thermal stress during service, and the feasibility of high corrosion resistance composite structure side sealing plate were discussed. The results show that thermal stress of the side sealing plate during service can be reduced by reducing the thermal expansion coefficient, elastic modulus and increasing thermal conductivity of the material. The higher the preheating temperature, the smaller the thermal stress. The suitable composition of carbon-containing materials can be compounded to the working surface of the side sealing plate to improve the corrosion resistance of the side sealing plate.
郭海荣, 李鑫, 李化龙, 施一新, 杨文刚, 李红霞. 薄带连铸用侧封板服役过程中热应力分析[J]. 中国冶金, 2022, 32(4): 27-33.
GUO Hai-rong, LI Xin, LI Hua-long, SHI Yi-xin, YANG Wen-gang, LI Hong-xia. Thermal stress analysis during service of side sealing plate for thin strip continuous casting[J]. China Metallurgy, 2022, 32(4): 27-33.
LIANG X,PAN F,ZHOU S,et al. Edge containment of a twin-roll caster for near net shape strip casting[J]. Journal of Materials Processing Technology,1997,63(1/2/3):788.
WANG Yu-fei,YANG Zhen-guo. Finite element analysis of residual thermal stress in ceramics-lined composite pipe prepared by centrifugal-SHS[J]. Material Science Engineering A,2007,460/461(15):130.